Electronics Forum | Tue Dec 27 10:00:19 EST 2005 | sparrow
Hello, does anybody have experience in thermosonic gold wire bonding to electroless nickel/immersion gold?? regards, Sergey
Electronics Forum | Tue Jun 13 04:42:26 EDT 2006 | yqdeng@gsl.com.hk
What is "Black pad"in ENIG(Electroless nickel/immersion gold), how to solve if it happen in SMD BGA solder joint?
Electronics Forum | Mon Mar 29 14:32:01 EDT 2010 | isd_jwendell
The board in the test "used an electroless nickel/immersion gold (ENIG) finish." If you are not using ENIG plating on your PCBs then you may not suffer from the same issue.
Electronics Forum | Tue Oct 21 21:34:56 EDT 2014 | davef
"Electroless Nickel Immersion Gold and Black Tar. What Is It and How Can It Be Prevented?" James Trainor, OM Group Electronic Chemicals, LLC SMTAI 2014 SUB2
Electronics Forum | Sat Oct 24 13:03:20 EDT 2015 | mikekeens
With regards to PCB surface finish I would recommend Electroless Nickel Immersion Gold (ENIG) because of the long shelf life, tarnish resistance, RoHS-compliance, and easy soldering compared to other surface finishes. http://www.surfacemountprocess.
Electronics Forum | Wed Nov 20 01:38:53 EST 2019 | ajspec
Hi, i'm facing solder mask peel off but limited to the solder defined pad only(opening area). no peel off on the other area and it happened on electroless nickel immersion gold finishing only. for other finishing is not affected. kindly advise if you
Electronics Forum | Fri Feb 09 20:05:15 EST 2001 | benefid
The ENIG process will yield between 3-7 micro inches (110 - 275 microns) of gold over the nickel barrier. This thickness range is pretty much the limit as this is a self limiting displacement reaction process. Once all surface nickel ions are repl
Electronics Forum | Tue Aug 20 18:15:02 EDT 2002 | davef
Haaaaa!!!! Soldering to plastic!!!! An apt analogy!!! I like to compare it to soldering to dirt. Some thing. In fact, you are soldering on nickel, when soldering on many things. It�s just that the gold, er Pd, flash enables the wetting mechanism
Electronics Forum | Tue Feb 01 09:53:58 EST 2000 | Ron Costa
I've been using the Electroless Nickel/Immersion Gold plating process for some time now. Here is what i know: It's very flat and solderable if you hold the board house to the following criteria: 120u inches of Nickel 4-9u inches of Gold What type of
Electronics Forum | Tue Feb 11 22:28:25 EST 2003 | davef
What do you mean by "new information"? On final module testing: * If you have hypercorroded nickel and you detect it during final testing, you'll notice it. * If you have hypercorroded nickel and you don't detect it during final testing, you'll ship