Electronics Forum | Mon Aug 16 20:32:10 EDT 2004 | davef
First, we didn't say "electrolytic soft gold with a minimum thickness of 5-8 of Au". We said, "'electrolytic soft gold' thickness 5 to 8uin". FOCUS. ;-) Second, we're unaware of an industry accepted specification that you can reference. IPC-2221
Electronics Forum | Mon Aug 16 18:09:33 EDT 2004 | Kris
ok I agree there has been a confusion with terminology When you say electrolytic soft gold with a minimum thickness of 5-8 of Au, is there a standard that you spec this from ?
Electronics Forum | Mon Aug 16 16:37:08 EDT 2004 | davef
As we mentioned in an earlier response in this thread [Q5], you do NOT want to solder to hard gold. Hard gold is a wear surface. [That's IT, that's the LIST.] If you want to solder to gold, then either use: * IPC-4552 ENIG specification, mentioned
Electronics Forum | Fri May 31 14:02:23 EDT 2002 | dougt
Russ We decided to use a PC-104 brd for a piece of equipment and had to make a "PC-104 Adaptor Brd" as it is affectionately known. The actual PC104 connectors came with what they called a solder system, a flat piece of solder with holes in it that w
Electronics Forum | Wed Aug 11 18:36:03 EDT 2004 | davef
90 Knoop. Q2: Thickness is 4 to 10 u" for Au and 300 to 400 u" for nickel A2: This looks like a ENIG spec. Although, the Ni is quite heavy, 150 uin is sufficient for most applications. [IPC-4552 ENIG specification: * Gold thickness of 0.075 - 0.125
Electronics Forum | Fri May 31 17:04:02 EDT 2002 | davef
We use boots / shunts er wutt ever you call them to protect solderable component surfaces from wave soldering. Not sure how it would work in your case try: * Kinnarney Rubber 450 Main St. P.O.Box 37 Mantua, N.J. 08051 609-468-1320 fax 7438 http://ww
Electronics Forum | Fri Nov 14 07:56:49 EST 2008 | davef
Section 9 of J-STD-001 gives you what you need. Further: * Flattened [coined] lead: http://workmanship.nasa.gov/lib/insp/2%20books/links/sections/files/711.pdf * Flat lug lead: Look for the Package Designator �LT� on page 7 of http://www.allegromicr
Electronics Forum | Fri Nov 14 02:18:04 EST 2008 | act_smt
What is the spec or true classification for the leads for an Electrolytic capacitor? Is it a : 1)Flattened coined lead??? or 2)Flat Lug Lead??? There is some confusion as to how we should be inspecting & accepting the toe overhang on these per IP
Electronics Forum | Tue Dec 02 07:56:40 EST 2008 | realchunks
Wow, rocket science with Nasa specs! I like it. I don't see the trick question here, so I'll continue.... IPC simply states over hang of round or flattened (coined) leads is acceptable (class 1, 2, & 3) if it "does not violate minimum electrical c
.gif)