Electronics Forum | Tue Jan 04 12:37:41 EST 2005 | Cmiller
We have been using this finish almost exclusively for fine pitch boards for about 5 years. Make SURE you use a board house that does the gold plating in-house. There are some potential issues as DaveF stated. The only problem we have encountered is w
Electronics Forum | Fri Oct 14 16:51:46 EDT 2005 | GS
It stands for Elettroless Nikel Immersion Gold, a kind of PCB finishing Entek (there are several kinds) is a brand name of an OSP (Organic Solderability Preservative)kind of PCB finishing. Regards............GS
Electronics Forum | Mon Jan 03 12:26:16 EST 2005 | barryg
We are looking at potentially doing a pcb that is enig finished as called out on its fab. drawing. We plan on a standard 63/37 water soluble paste. Is there any pro's and cons to this process with a pcb plated as such. What is the main advantage that
Electronics Forum | Tue Sep 14 10:10:39 EDT 2010 | teamcanada
We are having an issue with a PCB supplier. Their Tin HASL layer seems to be the problem. We have triedworking with them to correct their process. What seems to have helped is lowering their temperature of the Tin dip from 540 F to 510 F.We still ha
Electronics Forum | Fri Sep 17 03:13:00 EDT 2010 | grahamcooper22
In HASL pcb coating you need to fully coat the pads with solder and then blow off any excess solder to leave a nice coating on each pad. Generally pcb manufacturers try to give you a flat pcb pad to make your solder paste printing more consistent. To
Electronics Forum | Tue Oct 28 12:02:11 EDT 2008 | milas
Hi We have recently specified the following on a bareboard that has an ENIG finish. Does it sound about right or is it likely to give me problems ? Nickel : 3uM � 7uM Gold : 0.05 uM � 0.1 uM Thanks in advance
Electronics Forum | Mon Aug 08 22:32:18 EDT 2005 | adlsmt
If you are using fine lines and tight spacing ENIG may be cheaper than HASL. This is because there is not as much bridging at the board house between traces so they do less touch up. This would probably be even more true with no-lead. We have been us
Electronics Forum | Mon Jul 05 03:44:53 EDT 2004 | johnwnz
Dave, I'm going to disagree with you on the ENIG, it's my 3rd choice only just beating out OSP for that 4th spot. 1. Immersion Silver - cheaper than ENIG, as flat and no issues with Brittle interface (black pad) or Gold Embrittlement) Longer shelf l
Electronics Forum | Mon Feb 05 07:02:11 EST 2007 | CL
ASIR, Findings for us so far: OSP- has worked well for us for single sided boards only. We have seen problems with using it on double sided reflow applications. Also, some customers have specified OSP, but are intolerant of exposed copper. Limited
Electronics Forum | Fri Jul 13 12:32:14 EDT 2007 | rgduval
We've experienced this issue with SN100. A couple of things we've tried, all with varying levels of success: 1. Longer pre-heats. We use SN100 in a solder pot, and pre-heat the boards on our wave machine. This did have a positive effect, but I ne