Electronics Forum | Mon Feb 22 22:25:19 EST 2021 | rowan
Hi, We were having flux residue entrapment under the component. So we are evaluating to add steam cleaning with DI water, using precision micro prior to Di wash. Have anyone tried this and what are pros and cons. Your advice appreciated. Thanks
Electronics Forum | Mon Apr 05 08:25:31 EDT 1999 | ADRIANO FERNANDES
| | | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | | What disadvantages are there when using this flux? | | | Do you have any contact
Electronics Forum | Tue Mar 30 08:11:27 EST 1999 | George Steele
| | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | What disadvantages are there when using this flux? | | Do you have any contact detail
Electronics Forum | Mon Mar 29 09:33:37 EST 1999 | Chrys Shea
| I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | What disadvantages are there when using this flux? | Do you have any contact details with
Electronics Forum | Thu Jul 07 18:16:36 EDT 2005 | russ
What size discrete components and have you evaluated your pad geometries? If pads are too far apart this will happen. The flux resudue is simply there because you didn't solder the component. It will stay on top of the solder bump. You can see this
Electronics Forum | Sat Jan 29 05:43:51 EST 2005 | Chua
Hi Chunks, Thanks for your input. Appreciate you could send me a copy of your evaluation list as this type of evaluation is new to me..... Here is my email address :- pgchua@cyberway.com.sg Thanks.
Electronics Forum | Fri Jan 28 12:45:14 EST 2005 | Indy
That is what we call as good "Problem Solving Skills". :)
Electronics Forum | Fri Jan 28 01:56:32 EST 2005 | Chua
Hi, I could like to find out what are the things need to look out if I'm doing a new SMT solder paste ( water soluble & no-clean ) evaluation. And also flux ( spray type ) for wave-solder ( water soluble & no-clean ). Appreciate for all the input..
Electronics Forum | Tue Feb 01 20:08:39 EST 2005 | davef
Look here: http://www.epa.gov/ozone/snap/icel/noclean2.pdf
Electronics Forum | Fri Jan 28 12:29:01 EST 2005 | Bob R.
We use the exact same method Chunks outlined for evaluating just about anything we're going to roll out worldwide, whether it's a material or a machine. List your factors (print speed, solder spread, etc), assign each a weight, evaluate each paste a