Electronics Forum | Fri Oct 20 14:13:32 EDT 2000 | DENNIS XIONG
Dear all, We have a PCB design mistake that causes exposed copper layers on the edges of breakaway locations. Although we fixed the design, but we already made a lot of boards plus many made before we found the problem. I wonder if any one have some
Electronics Forum | Sat Oct 21 03:55:14 EDT 2000 | DL
Dennis, I've seen this before, and in our case we didn't need to seal the edges because there was no concern of shorting or anything in the end product, this is a choice you will have to make, Does your end product have any protrusions or mounting h
Electronics Forum | Thu May 18 03:15:32 EDT 2017 | wama
We are soldering wire 26AWG to jack socket. However after went through washing, baking, coating, curing processes the wire breaks (at joining point with jack socket) during wire dressing. We have tried to increase and decrease the solder amount but r
Electronics Forum | Tue Mar 14 12:56:07 EST 2006 | robhs
Q: Is anyone aware of any solderability issues that may exist when soldering beryllium copper parts (in this case spring contacts) to a PCB using standard Pb63/Sn37 solder paste/wire?
Electronics Forum | Thu Jan 23 23:00:42 EST 2014 | davef
I agree with AFlex. Don't tin stranded wire that's assembled into a screw terminal block. I believe the reasoning has to do with avoiding stress on the wire metal caused by different expansion rates of the solder and the wire. BR davef
Electronics Forum | Thu Jan 23 08:08:10 EST 2014 | charliedci
Should stranded copper wire (20 gauge 19 strand) be tinned prior to insertion into screw connector? One of our customers "suggests" tinned, but past experience tells us no.
Electronics Forum | Thu Jan 23 08:18:07 EST 2014 | aflex
Even for me its a No. Its quiet strange why some preferred tinned ones.
Electronics Forum | Wed Nov 02 01:24:07 EST 2005 | arnold
we are encountering a problem on our production. after dipping a copper wire AWG#30 to a leadfree solder the wire becom thinner and easily to break. does the leadfree soler has the capability to weaken the wire (lessen the diameter)after dipping to l
Electronics Forum | Thu Jan 29 05:13:35 EST 2015 | neeraj_iiser
how to solder manganin 0.05mm manganin wire to a copper plate
Electronics Forum | Wed Nov 02 01:30:12 EST 2005 | fctassembly
Hello Arnold, Yes, by definition of joint formation, copper will dissolve in lead free solder in order to form the connecting intermetallic layer. There is a distinct difference in the copper dissolution rates of the major alloys being considered wi