Electronics Forum | Wed Dec 28 16:03:53 EST 2005 | Chris
I have lots of experience with thermosonic gold ball bonding. You can read the literature and you will probably find some papers that say you can do it. I have never been able to do it. We gold ball bond all day long with little problems at all bu
Electronics Forum | Tue May 13 06:57:10 EDT 2003 | davef
Your vendor site is totally correct. 2Ag is an excellent solder, but it does nothing to prevent tin and gold from reacting chemically. An earlier poster is correct gold goes into solution in liquid solder very fast, less than a second. Gold and ti
Electronics Forum | Fri Apr 13 21:02:19 EDT 2007 | Sam
Anyone experience using SnPb wire to gold plated ICs? I have tried to solder the SnPb wire to the gold plated ICs lead, but the surface finishing is dull. Can anyone explain that to me? Why it is not shinny surface? Any recommendation?
Electronics Forum | Mon Apr 16 09:12:23 EDT 2007 | davef
Standard for appearance: J-STD-001 and IPC-A-610 committees eliminated the requirement that solder connections be "bright and shiny". Certain solderability protections; such as Au, NiPd, NiPdAu; can affect the surface texture of a solder connection,
Electronics Forum | Tue May 19 10:23:06 EDT 1998 | Mike C
| Howdy Richard, | Welcome to the club! I now dub thee a full fledged member of the "Spotty Gold Finger and Bleeding Ulcer Society"...or SGFBUS for short... (GRIN) | I know it's not funny to be in that position, but there's so many different places t
Electronics Forum | Tue Mar 21 20:25:30 EST 2000 | Dave F
John: What�s the matter? Free gold � good thing for you, bad thing for your supplier. :^) Pre-tinning of gold plated leads is important to: � Prevent gold embrittlement of the solder joint � Determine if the leads are solderable prior to assembly (
Electronics Forum | Wed Dec 22 01:39:06 EST 2010 | boardhouse
Hi Johan, As a Asian board supplier - I would not recommend using Lead free hasl on any product that has BGA, you would be just looking for issues, flatness being the main. I agree with one of the other replies - Your purchasing dept. should not be
Electronics Forum | Mon Feb 27 09:09:36 EST 2006 | davef
Silver on your copper or brass part is a solderability protection. The silver diffuses into the solder and you solder to the base metal, either the copper or brass in your case. Soldering to copper is well known. The issues are soldering to brass
Electronics Forum | Thu Nov 30 16:10:05 EST 2006 | Hussman
Wow, why all the anger? This gap you guys are talking about is measured as "G" in IPC/EIA J-STD-001 (Chunks was there, but she failed to read the fine print). And almost all parts that measure G follow Note 3 which states "Properly wetted fillet s
Electronics Forum | Tue Jun 04 17:10:13 EDT 2002 | davef
First, �flash gold� is very loose language. It means different things to different people. �Flash� gold is a thin coat of immersion gold. Imm gold self-limits at ~0.3um[12uin]. And fabs put-down �flash� prior to electroplating thicker gold for wi