Electronics Forum | Thu Dec 08 08:18:29 EST 2005 | grantp
Hi, We have recently moved to flash gold as well, as we had solderability issues with emerson gold, and this was supposed to be a solution. However I did not know flash gold would be thicker, and could have other issues. Is flash gold a stable boar
Electronics Forum | Fri Sep 21 10:35:37 EDT 2012 | davef
Flash gold is just thin electrolytic gold plating over electroless nickel or electrolytic nickel. Flash gold plating ... * Less than 3 microinch thick will be porous and take solder poorly * Greater than 10 microinch thick will cause brittle solder c
Electronics Forum | Fri Mar 24 18:07:25 EST 2006 | Chris
Flash gold is just thin gold plating over electroless nickel or electrolytic nickel. Flash gold is electrolytic gold where the panel is connected to a plating rectifier and current causes the plating process to occur. Gold thickness is controlled b
Electronics Forum | Mon Feb 04 16:45:40 EST 2002 | bdoyle
Saying "yes" to that dialog box shouldn't have any adverse effects. Its just the flash player (I thought 5 was the latest version) .It is for some of the newer ads that are appearing. By switching to flash for many of these banners we are able to l
Electronics Forum | Fri Dec 16 07:42:05 EST 2005 | pavel_murtishev
Good evening, We noted one more very strange problem with flash memory chips. Device fails test due to flash chip malfunction. From the first sight open joint or cold joint can cause such problem. But all chip legs are soldered well. We just heat th
Electronics Forum | Fri Mar 24 15:44:11 EST 2006 | Hoss
I have no experience with soldering to a flash gold finish. We have specified ENIG for a prototype PCB order and the supplier is asking us if they can use flash gold. They are telling us that the two are interchangable which I don't believe. The
Electronics Forum | Wed Apr 03 20:23:44 EDT 2024 | lremme
I tried to clone my cfi-128 flash memory card, but can't get it to boot. I am concerned because I have no backup if the original Flash card stops working. Does anybody have a flash card with Topaz-x VIOS and (MSDOS 6.2) preloaded? I would be looking
Electronics Forum | Fri Sep 06 14:03:18 EDT 2013 | horchak
If you are a CEM you are setting yourself up for failure and will be left holding the bag. Flash gold has one purpose. It is a protective coating for the base medal to keep it from oxidizing. It is very thin and will be absorbed into the solder joint