Electronics Forum | Wed Aug 10 07:55:21 EDT 2005 | ajaydoshi
we are using heareous F381, F352 no clean solder paste. specially in qfp for high frequency board we observe that cleaing / removing of ' no clean flux 'is require. if we do not clean same most of time after all test & envioumental test it shows pin
Electronics Forum | Tue Dec 11 10:12:36 EST 2007 | George
Hi everybody, Is there any criteria as far as No-clean flux residues surrounding solder joints when using selective solder machines? I have a Novastar SPA 400 and use flux NC kester 959. If I decrease the amount of flux, then I experience problems w
Electronics Forum | Sat Jan 10 10:28:06 EST 2004 | tommy
Is it possible to have zero flux or paste spattering for all smt reflow pcbs. We are seeing around 0.4% of flux spattering and looking forward to zero defect.
Electronics Forum | Fri Dec 16 10:25:37 EST 2005 | solderiron
Rather than cleaning a water soluble flux residue off the board, by encapsulating the product. covering the board or the component with lets say a Hysol encasulant. Would this prevent the active flux residue from migrating and deteriorating the elect
Electronics Forum | Wed Sep 05 14:53:45 EDT 2001 | Jeff Meier
We have customers that are requiring no flux residue left on boards after soldering of non-water washable parts. We currently use Multicore Crystal 502 No-Clean to solder parts that are not washable. Has anyone come up with a good way to remove this
Electronics Forum | Wed Aug 10 08:10:39 EDT 2005 | davef
Comments are: * Sounds like it's necessary to clean "heareous F381, F352 no clean solder paste" in your application. Consider a paste that may be better suited to your application. * If you're cleaning "low residue flux", consider using an organic ac
Electronics Forum | Fri Oct 10 05:04:26 EDT 2008 | bing007
We are using Mulicore MF101 flux and a Vitronics selective soldering machine on a lead-fee assembly and are having trouble with nozzles blocking even when the nozzle aperture is increased. Has anyone come across this problem before using fluxes with
Electronics Forum | Wed Apr 03 19:03:31 EDT 2013 | hegemon
In agreement, in that you should have already printed enough paste on the board to accomodate the joint. Adding paste would give the result you described. (too much solder) Adding a little flux (only) and heat would be the correct path out of that s
Electronics Forum | Tue Apr 02 13:27:41 EDT 2013 | ericrr
So where does one get good flux? the engineers had a little bottle of good flux that the owner of the company liked, it had a oily feel to it. So then the company purchased some more since the engineers look like it was about to run out, the owner of
Electronics Forum | Wed Jan 14 06:42:38 EST 2004 | tommy
We see spattered(spitting of flux or solder to nearby area) solder/flux on gold fingers.We view the gold fingers area under 30x before reflow and it is cleaned but after reflow we see flux droplets or solder on gold fingers. We tried to changed a new