Electronics Forum | Thu Jun 26 13:55:56 EDT 2008 | dyoungquist
Water will not remove no clean flux residues because they are not water soluble. Solder paste with no clean flux should only be used when the assemblies do not need to be cleaned. That said, you can buy special cleaning solvents specifically for re
Electronics Forum | Wed Jul 21 17:49:52 EDT 2004 | jsk
problem: Too many solvents and boards are not clean Flux remains on the board after vapor degreaser and "Powdery" white residue after vapor degreasing Flux type is kester 186 Process: hand solder High Temp alloy, spot clean after hand solder e
Electronics Forum | Wed Aug 10 08:10:39 EDT 2005 | davef
Comments are: * Sounds like it's necessary to clean "heareous F381, F352 no clean solder paste" in your application. Consider a paste that may be better suited to your application. * If you're cleaning "low residue flux", consider using an organic ac
Electronics Forum | Mon Jun 19 09:47:23 EDT 2017 | georgetruitt
You have a lot to think about! What does the flux manufacturer recommend as far as specifics like water temp or pressure? Do they recommend high temp di-water a detergent or saponifier? Do you currently have a cleaning machine, batch cleaner or inl
Electronics Forum | Fri Jul 23 14:41:41 EDT 2004 | Steve Stach
Dear JSK, It sounds like the root causes of your problem are two fold. First, excessive heat will polymerize the abietic acid found in rosin forming neo-abietic diamers and polymers which are much less soluble than the parent monomer. There are
Electronics Forum | Fri Apr 22 05:01:19 EDT 2011 | azrina
Hi, I am doing my master degree in flux cleaning process for flip chip assemblies and required to establish a new receipt for flux cleaning. currently, i am doing screening process for the parameters involve ; temp,pressure, surfactants, speed and a
Electronics Forum | Fri Apr 22 10:50:51 EDT 2011 | blnorman
Quick question, how are you measuring the effectiveness of the cleaning process to remove the flux?
Electronics Forum | Thu Mar 17 22:14:42 EST 2005 | Chua
Hi Davef, Thanks for your advise...... We are running no-clean process. If there is white residues after few days.....is it cause by those excess flux. Thanks
Electronics Forum | Thu Mar 17 10:14:30 EST 2005 | davef
If you're washing the boards properly, you should see any problems, maybe a little extra floaming, but that won't be too bad. If you're running no clean, you need to aplly flux according to your supplier's recommendations. If you decide not to foll
Electronics Forum | Wed Apr 28 12:08:02 EDT 2010 | tjg
Our latest designs are flip chip on flex based and we have issues with delamination/blistering. We know it is related to our vapor solvent (n-Propyl Bromide based) attacking an inner layer adhesive. Has anyone else ever heard of something like this?