Electronics Forum | Wed Apr 04 08:45:37 EDT 2007 | meritajs
Hi, colleagues! We only start using pb-free tehnology Our wave have foam fluxer What kind of flux would be best if we will use Sn100 solderbar What is your experience Best regards Peter
Electronics Forum | Wed Apr 04 10:48:25 EDT 2007 | pjc
Indium Corp. has some, 3549-HF and 3590-T, both are OK for foaming. Most of the better performing newer fluxes require spray application for best performance. Alpha, Kester and others have wave fluxes too. http://www.indium.com/products/circuitboar
Electronics Forum | Thu Jun 28 09:40:49 EDT 2012 | austinpeterman
We just stepped into the inline wash world with a techical devices new clean galaxy plus. We are noticing a significant amount of foaming when washing our boards after selective solder. One theory is that the water soluble flux used is not being cu
Electronics Forum | Mon Jul 02 18:40:33 EDT 2012 | joeherz
We used to have a Nuclean 324 that was running closed loop with a DI water recirc system. We also had problems with foaming that was solved with a relatively simple fix. We bypassed the final rinse solenoid so that it was always running. This allo
Electronics Forum | Thu Jun 28 16:02:05 EDT 2012 | allwave
We had a similar problem with foam in our inline cleaner (TD). The problem were the solder paste flux residues. Boards went straight from SMT to Wave process and then washed. Anyway we changed the solder paste and problem solved. Are you using saponi
Electronics Forum | Fri Jul 18 15:25:19 EDT 2014 | davef
The presence of agitation at an air / solution interface and a foaming agent causes foaming. Most water soluble fluxes contain surficants. Surficants are foaming agents. First, it's likely this foaming is caused by poor control of the temperature of
Electronics Forum | Fri Jul 18 12:16:06 EDT 2014 | island2013
I had the same situation at a facility a few years ago. We moved our wash from one building to another and it was fine for months and then we had the foaming issue similar to yours. We tried everything from adding anti foam agents to even having th
Electronics Forum | Wed Jul 16 14:21:15 EDT 2014 | toddp2012
Hi all, we have a Speedline Technologies ELEOCTROVERT/Aquastorm 200. In January we stared supplying it with pre-filterd to the DI cabinet next to machine so our large media would last longer. All was fine for about 4 months and then we started gett
Electronics Forum | Wed Apr 27 08:19:41 EDT 2011 | charliedci
We are in the process of changing over our wave solder flux from alcohol based no clean to VOC free water based no clean. We are running an old Eletrovert with foam fluxer, tin lead solder. After preliminary testing on scrap boards and now starting t
Electronics Forum | Mon Nov 12 12:59:19 EST 2007 | ck_the_flip
Here are the scenarios: *No-Clean Flux & Foam Fluxer: alcohol is used as a thinner (for titration purposes) if your flux is alcohol-based *No-Clean Flux & Spray Fluxer: alchol is used only as a cleaning agent for your sprayhead.