Electronics Forum | Tue Sep 21 13:10:10 EDT 1999 | Dave F
| Dear All, | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | I mean that I wonder why we use
Electronics Forum | Wed Aug 11 07:41:52 EDT 2004 | gregoryyork
Check cure of solder resist. Use a No clean low solids rosin flux this will stop problem. Should see almost zero solder balls if put through a single wave compared to a dual wave. If this is true then it is a resist issue and cannot 'resist' the sold
Electronics Forum | Wed Sep 22 02:45:23 EDT 1999 | Brian
| | Dear All, | | | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | | | I mean that I wonder
Electronics Forum | Fri Oct 10 05:04:26 EDT 2008 | bing007
We are using Mulicore MF101 flux and a Vitronics selective soldering machine on a lead-fee assembly and are having trouble with nozzles blocking even when the nozzle aperture is increased. Has anyone come across this problem before using fluxes with
Electronics Forum | Tue Jan 23 23:28:54 EST 2007 | jovial_guy23
If you have flux deposits on the cooling plates, try out Zestron's VIGON RC101...It is an extremely good product especially for reflow ovens and wave solder systems. Check it out...Minimal maintenance water based chemistry with no flash point...Much
Electronics Forum | Thu Sep 06 10:55:37 EDT 2001 | davef
saturation occurs at ppm levels. Remember, IPA is extremely flammable and its bulk use makes the plant liable to all sorts of quite repressive safety rules/regulations and so on. Ignoring these rules exposes the owner to fines and possible plant cl
Electronics Forum | Wed May 19 11:01:17 EDT 1999 | Vince Whipple
Wes, I have been involved with many customers changing over from an alcohol based no-clean to a VOC-free process. The change-over can be made easier by such things as air movement, convection preheat, "drains" or reliefs in pallets (if used), contr
Electronics Forum | Thu Apr 05 16:57:58 EDT 2001 | Jerry
Hi Dave, If my solder paste is RMA based and my Wave Solder flux is NC Based, will there be incompatibility problem that might arise during the process? thanks
Electronics Forum | Thu Apr 05 17:00:43 EDT 2001 | Jerry
Hi Dave, If my solder paste is RMA based and my Wave Solder flux is NC Based, will there be incompatibility problem that might arise during the process? And if i don't clean my boards what will be the possible effects of the residues left? thanks
Electronics Forum | Mon Oct 08 21:05:00 EDT 2001 | ksfacinelli
DO NOT Mix Technologies.... If you are using a no clean solder paste use a no clean wave solder process. I have direct experience with using a no clean paste and a RA water-soluble wave solder process. When cleaning with the water wash system your