Electronics Forum | Wed Jun 11 16:30:33 EDT 2003 | T.Vick
You have received some great feedback so far. I would like to summarize and add a few points regarding maintenance. You should start (as recommended already) by verifying your component library data. Using the default values from the master library i
Electronics Forum | Fri Mar 18 15:02:07 EST 2005 | pmd
Please clarify, Z axis gears (Blades)? The MPM head I believe is what your are asking is driven up and down via a lead screw. The machine gets the zero point from the "HAT" tactile sensor in the table nest. When squegees are installed the blades are
Electronics Forum | Tue Jun 05 17:31:08 EDT 2012 | swag
Do you see any issues with grid lock on double sided boards? My concern is that you set it up for the first board second side (populated side down) then you might have parts that aren't exacly at the same height on the next boards due to shifting or
Electronics Forum | Mon Apr 28 02:22:52 EDT 2014 | jkhiew
We found repeated pad lifted after different SMT Reflow temperature (eg: 243 deg C and 233 deg C) at an isolated slot. The PCB Supplier had claimed that such condition is acceptable as per IPC 600H Clause 3.3.2 (Cross Sections) - eg: Acceptable - C
Electronics Forum | Mon Apr 28 15:20:50 EDT 2014 | davef
Your customer is correct. Your supplier has clamped some sort of machine to your butt and has plugged it in the wall outlet. Honest mistake: * IPC-A-600H, 3.3.2 Lifted Lands - (Cross Sections) ... pertains to boards that were cross sectioned after t
Electronics Forum | Tue Jan 16 20:34:17 EST 2007 | davef
DAVE�S BOOKSHELF ASSEMBLER�S ESSENTIALS Title: Soldering in ElectronicsAuthor: RJ Klein WassinkPublisher: Electrochemical PublicationsISBN: 090115024XPublication date: December 1989 I know, I know. The book was written in 1989!!!! I use this b
Electronics Forum | Wed Dec 03 16:16:18 EST 2008 | grantp
Hi, Ok, and thanks for the heads up on that, and I will contact them and see what model that is. I liked one of their manual printers, as it looks like the board slides back on linear bearings and then lifts up under the stencil, instead of the usua
Electronics Forum | Mon Jun 18 13:29:34 EDT 2001 | nifhail
What is the recommanded profile for board which consist of 0402 & 0201 comps. to reduce the effect of tomb-stone. Slow ramp rate ? how slow is considered as slow. Soak time 60 or 120 C,at which end should I stick to? what is the best time before reac
Electronics Forum | Wed May 21 04:50:51 EDT 2008 | aj
Hi all, We had similar problems a while back. Boards would fail at test but if you applied pressure to the BGA they would pass. Turned out that during the PTH assembly process the Operators were flexing the cards during the insertion of an Oupin C
Electronics Forum | Mon Nov 06 10:29:28 EST 2000 | Dean Stadem
All of the replies have merit. Here is another one. Because the cause of the tombstoning is wetting forces that are imbalanced, and one end wets faster or more readily than the other, the 0402 lifts up on that end easily because of its low mass. Incr