Electronics Forum | Tue May 30 22:43:35 EDT 2006 | zoedujuan
Hi,see you message on forum. and you said you install a ESD flooring for a Germany company,I guess your company do the ESD antistatic products,and my company do this kind of products,do you have the interesting to buy them with good quality and comp
Electronics Forum | Fri Feb 24 15:15:33 EST 2006 | russ
The No-Clean indium lead free paste runs well. We discontinued because of extremely high shipping costs. We can get the same results with cheaper product. Almost all of the discussion in this forum about SAC305 and SN100C have to do with wave sold
Electronics Forum | Wed Mar 15 17:52:37 EST 2006 | russ
Set points are unique to each individual oven. You cannot tell anything with the setpoints at the zones. your profile is a soak profile most likely. Suspicious ..... Absolutely! Flux activation is not important and neither is the temp of the boar
Electronics Forum | Tue Apr 04 13:45:11 EDT 2006 | ultraspray
My name is Stephanie Baldwin. I work for USI and have been following this forum. I would suggest that you give both USI and Asymtek the opportunity to coat a sample board for you. You can then compare the two technologies side by side. If possibl
Electronics Forum | Fri May 19 17:56:08 EDT 2006 | jbrower
Look buddy. Pay for an advert like everyone else. He asked for tips and hints on the change over he did over the weekend. I'm sure that if he wanted to talk to you he would have. Please don't polute this forum with what amounts to junk mail. Your
Electronics Forum | Wed May 24 16:47:21 EDT 2006 | patrickbruneel
Inds, It's about time that lead-free components can stand higher temps "myth" stops. The only difference is the plating, the component itself has not changed. Can you give us an update on this threat? If you�re the same inds http://www.smtnet.com//
Electronics Forum | Thu May 25 08:58:14 EDT 2006 | inds
aj, check out the link http://www.smtnet.com/forums/index.cfm?fuseaction=view_thread&CFapp=8&Thread_id=10387&mc=5 as Samir mentioned in that link, try keeping your peak temp within 220-225degC.. TAL 217 around 20-40 sec..depending on your ball d
Electronics Forum | Fri Jun 09 07:58:54 EDT 2006 | samir
Guru/Moonman, Shocker, and Wave Master (who seems to have made a comback of sorts) make this blog entertaining and inject some much needed humor on the forum. Let's face it, guys. There's a nerdy Napoleon Dynamite in all of us, and most of you gu
Electronics Forum | Wed Jun 14 21:56:07 EDT 2006 | davef
Stencils should be cleaned frequently enough to ensure total removal of any bottom side residues, but not so infrequently as to allow the same residues to dry or cake on, making their removal much more difficult. Look here: http://www.smtnet.com//fo
Electronics Forum | Fri Jul 28 21:58:44 EDT 2006 | Wave Master Larry
All you funny guys and your names. Listen, this is whats wrong with this forum and the world today. Too many clowns making fun of serious buisness. What the hell is POD group anyway. Sounds like some outer space movie to me. Maybe they hung up o