Electronics Forum | Thu Jun 08 22:54:31 EDT 2006 | hunghung
Dear all, If a PCB board, 2 mils of core with 1oz copper at the top and bottom, is it a good board to be fabricated? will it be caused warpage during etching for inner layer process? if yes, what is the real factor caused to warpage? How to solve t
Electronics Forum | Fri Jun 09 15:41:59 EDT 2006 | shawnvike
That is the problem I am having! Except with 3 separate manufacturers. To answer some of the other questions... Baking - diligence Stencil - as far as we can tell it is good Placement is good We are using Pb-free parts and solder, but I have see
Electronics Forum | Tue Jun 13 16:45:30 EDT 2006 | adlsmt
If the only difference is the layer count, check the profile as stated above. If you dont have a profiler you can probably get the local Kic or Mole rep to do a demo on that board. I believe I was the one who stated in an old post that prying the lea
Electronics Forum | Fri Jun 09 10:04:16 EDT 2006 | Rob
I know it's friday afternoon, and it's actually hot for once in this country, so my brain may not be working properly here, but isn't 30 micro inches of gold about 0.75 Microns? So that's dead in the middle for gold plating thickness (like gold finge
Electronics Forum | Mon Jun 12 10:07:08 EDT 2006 | mkehoe@sipad.net
Can someone look this over and see if this helps?? ****************************************************** I read the e-mail threads and I think the respondents are all mixed up on the units of measure. the print reads: Gold Plate (80 mocroinches m
Electronics Forum | Sun Jun 11 21:40:21 EDT 2006 | Wave Master Larry
Grant, I beleive your problem may lie in the top side heater. Only 60% seems too little. I need to run my Soltec way past 60% to get top side wetting on larger part. You may want to have someone fix that. Perhaps Dr. Bocephus H good time budwies
Electronics Forum | Mon Jun 12 19:33:12 EDT 2006 | grantp
Hi, Thanks, and we are doing that today. After spending the day playing with all the usual things that used to work, we are focusing today on profiling and data to get things right. The only worry I have is did we get a wave that can handle this, a
Electronics Forum | Thu Jun 15 19:39:43 EDT 2006 | Bolos
nice to hear from you..my company is an ems.so need a more flexible reflow.. we have 3 lines and soon to install another line for leadfree ideally..so.. its getting a new one hopefully..a seven zone actually i think might do the job... for the wave i
Electronics Forum | Fri Jun 16 14:54:21 EDT 2006 | jbrower
Howdy Bolo, I see. I currently run a 5 zone 1500 Heller, It's a very nice reflow oven and one of my favorites. Hopefully in July we will be getting in our 1700 from Heller. These reflow ovens (used) can be had for a pretty decent price at least in
Electronics Forum | Mon Jun 12 10:46:37 EDT 2006 | mhanc
I am trying to help a customer with a problem. His Process Tech is out and the operator is trying to load a program via floppy. When trying to load on the Amistar 5630 the following errors occur: Data Type Error (level.4) we continue to load and