Electronics Forum | Thu Jan 17 20:33:05 EST 2002 | ianchan
Hi, Can anyone help explain the benefits/disadvantages of bareboard pcb baking, as part of the pre-heat conditioning, before the bareboard pcb use in SMT production run? The pcb board is 200mm x 240mm panelized pcb board, and has 28 smaller pcb boa
Electronics Forum | Sat Jan 19 02:29:11 EST 2002 | ianchan
Thanks for the tips... found out the ex-employee guy, had pre-bake conditioning put into the process flow, as this pcb is made of polymide material, that is reputed to have historical patterns in thermal sensitivity. To avoid "thermal damaging" the
Electronics Forum | Mon Jun 28 09:15:21 EDT 2004 | jdumont
Morning all, we have been seeing some problems with the edges of some of our BGA's curling away from the PCB after reflow. Is this possibly a moisture problem? If so what would be a good time/temp to bake them at to rectify the problem? Thanks in
Electronics Forum | Fri Jan 18 04:45:32 EST 2002 | wbu
Ianchan, baking as being part of pre-heating is obviously sensless cause the PCB will not maintain any of that heat till soldering. Common reason for prebaking PCB�s is getting the moisture out to prevent outgassing, warpage and maybe other defects.
Electronics Forum | Wed Apr 23 19:00:39 EDT 2008 | stevek
It depends on the laminate but a PWB is like any other MSL component. Some fab shops are only waranting standard FR4 laminates for 45-60 days when processed at lead free temperatures. The best thing I can say is to try some weight gain/loss experim
Electronics Forum | Thu Aug 24 15:54:13 EDT 2006 | davef
It depends. What is: * Storage environment and period * Board laminate, epoxy, and copper thickness of PTH * Down stream process * Etc FR4 0.062" thick boards absorb between 0.08 to 0.1%Wt of moisture within a 24 hour period, and 0.2 to 0.23%Wt in
Electronics Forum | Wed Jan 13 04:27:00 EST 2016 | crystalpcb
Hi Here is our factory production capability: Shenze Electronic PCB Specification Layer Count 1 to 35 Layers Material Brand Shengyi,KB,GRACE,ISOLA,Rogers,Taconic,ARLLON,Bergquist Base Material FR-4（TG135,TG150,TG170,TG180），Halogen Free FR-4，Ceramic
Electronics Forum | Thu Aug 09 09:05:09 EDT 2007 | davef
There are no requirements acceptance criteria for baking of board assemblies. What are your customer requirements? The common reasons people choose to bake PCB are to prevent: * Delamination of multilayer boards * Measles, particularly on double si
Electronics Forum | Thu Aug 16 13:00:32 EDT 2007 | russ
Here is what you need to do if you can, Since you want to shporten the bake time you need to increase temp. weigh a board prior to your current bake process (you need very hi resolution scale for this) weigh the same board after current process a
Electronics Forum | Sat Jul 26 11:17:31 EDT 2008 | manishc
i am facing problem of pcb track lifing at B.G.A. after reflow.we r using lead free paste and fr-4 grade pcb with peak temp.about 270 deg.
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.png)
winsouce.jpg)