Electronics Forum | Mon Jul 13 11:38:16 EDT 1998 | Steve Gregory
Zulfiqar, The company that makes these stencils is a Canadian company named KJ Marketing (I'll paste a link to the web site in this message). It sounds pretty interesting. I've communicated with a few people that have used these stencils and the
Electronics Forum | Wed Dec 18 15:38:59 EST 2002 | swagner
I have had a similar problem in the past, since I have never worked with a semiautomatic printer there could be a few things I recommend that will not work for you. 1. Make absolutly sure that you have proper support under all of the BGA's. 2. Print
Electronics Forum | Sun Dec 22 06:00:54 EST 2002 | Mark
Hi: Your stencil specs are good; Did you check the stencil thickness? It would be worth a ck since there may be an error from the stencil mfr If the paste is not releasing with good stencil specs, these are possible causes: 1 The paste isn't tou
Electronics Forum | Wed Jan 22 13:17:48 EST 2003 | slthomas
We're considering stenciling SMT adhesive to increase throughput. This is an as-of-yet unproven process and for that matter pcb design (we've never done anything with more than about 50 SMT parts on the bottom, this board has in excess of 1200, but
Electronics Forum | Fri Oct 22 11:53:53 EDT 2004 | C Lampron
Hi Christina, What would you be basing the yields off of? Is it solder defect, component placement, etc....? I have worked for a flex house for quite a few years. You are right. The Polyimide is very dimentionally unstable. (even more so on humid da
Electronics Forum | Thu Jan 06 06:15:49 EST 2005 | mattkehoe
We need some opinions about a situation that is causing problems in our process. The pcb's in question are .125 thick with a HASL finish. The boards are coming in with a large amount of solder trapped inside the via holes. Sometimes this solder is ac
Electronics Forum | Tue Jan 25 09:15:02 EST 2005 | Marc A
Good info, thanks for passing along. The company I work for (equipment supplier) ran some tests with lead free material in air and N2 environements for reflow. In the air reflow environement it was noticed that the material does not spread, much li
Electronics Forum | Wed Apr 19 16:43:05 EDT 2006 | samir
Silicone-based coatings "repel" most foreign,non-compatible materials like peelable solder mask, and rubber or vinyl boots. The result is, uncured material around the vicinity of where the boot was. Trust me. Been there and done that. As a rookie
Electronics Forum | Fri Jun 18 15:37:44 EDT 2010 | remullis
One thing I have run into when placing cap's flush to the board is blow holes due to the plastic sheathing used around the cap. It would form a gasket going through wave and exhaust out of the holes therefore blowing the solder out with it. This cap
Electronics Forum | Mon Jun 04 23:52:57 EDT 2012 | rway
Actually, if you experience lack of witness marks, you probably have a problem. Witness marks are OK and will not affect your assembly. I assume this is an SMT assembly we are talking about, in which case, this is what your test pads are for. You
ORION provides innovative solutions to our customers' EMI/RFI Shielding, Insulating, Screening and Sealing needs in a broad spectrum of manufacturing environments.
Manufacturer / Distributor / Consultant / Service Provider
1 Orion Park Drive
Ayer, MA USA
Phone: 978-772-6000
.gif)
.gif)
winsouce.jpg)