Electronics Forum | Tue May 29 16:02:36 EDT 2001 | genny
500 insertions � 50 m gold => 300 insertions � 30 m gold => 50 to 75 insertions � 20 m gold => 10 insertions. " Dave stated that the 'm' referred to micro-inches. I could probably insert this board 1000's of times without a problem. Am I missing so
Electronics Forum | Fri May 31 08:51:09 EDT 2002 | zanolli
Hello Dave, As related to connector mating interface, fretting corrosion is the oxidation of the contact points, causing high resistance across the interface. Fretting corrosion is caused my micromotions in the interface exposing the metalized conta
Electronics Forum | Wed Aug 11 18:36:03 EDT 2004 | davef
90 Knoop. Q2: Thickness is 4 to 10 u" for Au and 300 to 400 u" for nickel A2: This looks like a ENIG spec. Although, the Ni is quite heavy, 150 uin is sufficient for most applications. [IPC-4552 ENIG specification: * Gold thickness of 0.075 - 0.125
Electronics Forum | Sat Apr 10 11:47:16 EDT 2004 | mskler
Hi all, When we are producing A gold Plated PCB Then the Prob Of Dry soldering is coming Profile temps are 130, 150, 180,and 220 top & 215 bottom.Then what are the other causes or Precautions may be taken.
Electronics Forum | Mon Mar 30 03:10:44 EST 1998 | Patrick Ng
Hi, We have encountered de-wetting issues with gold plated components( SMT LEDs ). The problem comes and go and we yet to locate the root cause ( process, component or solder paste etc ). The rest of the components on the boards are not having this
Electronics Forum | Sun Apr 11 14:35:25 EDT 2004 | davef
Please: * Describe the color and texture of the dry solder connection on the board. * Tell us the thickness of the gold and nickle plating on the board pads. * Inform us about the width and scope of the problem.
Electronics Forum | Mon Mar 30 07:41:06 EST 1998 | Earl Moon
| Hi, | We have encountered de-wetting issues with gold plated components( SMT LEDs ). | The problem comes and go and we yet to locate the root cause ( process, component or solder paste etc ). | The rest of the components on the boards are not havi
Electronics Forum | Mon Apr 12 08:53:12 EDT 2004 | russ
what kind of temps is the board seeing? I noticed zones at 220 and 215 respectively could you be running too cold in the oven? Russ
Electronics Forum | Mon Mar 30 12:55:16 EST 1998 | Justin Medernach
| Hi, | We have encountered de-wetting issues with gold plated components( SMT LEDs ). | The problem comes and go and we yet to locate the root cause ( process, component or solder paste etc ). | The rest of the components on the boards are not havi
Electronics Forum | Fri Apr 13 22:38:19 EDT 2001 | edylc
Hi , Could you be seeing the nickel under the gold plating because you are removing some of the Gold with the Kapton Tape....?? You mean , the adhesive properties of the kapton tape will cause the gold plating on the gold finger to be somehow peel of