Electronics Forum | Fri Apr 13 13:45:25 EDT 2001 | gsmguru
Just a guess-- Could you be seeing the nickel under the gold plating because you are removing some of the Gold with the Kapton Tape ? This should be easy to verify. Otherwise it sounds like things are pretty much covered.
Electronics Forum | Thu Jul 15 16:29:49 EDT 1999 | Charles Morris
We are currently assemblying several different board type with gold plated lands with varying results. Can any of you that has successful experience in this area give me some pointers. What paste do you use? Do you use the recommended reflow profi
Electronics Forum | Thu Nov 09 23:27:53 EST 2000 | Craig
We are considering using gold plating on our fine pitch pcbs (as oppossed to HASL). We have heard of long term solder reliability problems with joint imbrittlment how bad is this and does it apply for all of the different plating processes the same?
Electronics Forum | Thu May 02 09:33:30 EDT 2013 | 15009
Looking for advice on soldering lead free paste to a board with very heavy gold plating. I have learned from the Customer that this is HARD GOLD and that it is 10-20 Micro Inches Hard Gold over 100 Micro inches of Nickel. When we reflowed the solde
Electronics Forum | Tue Apr 17 21:30:27 EDT 2001 | davef
The issue is on the table. Which is it? Are you ... * Loosing your gold plate when you remove the tape? [A tape test is a standard test for evaluating gold fingers. Check IPC-TM-650, test number wachacallit. Checkitaut.] OR * Putting tape o
Electronics Forum | Fri Feb 28 01:08:33 EST 2020 | sarason
Back in the 50's, 60's and 70's gold plated boards were all the rage for high reliability. test equipment, milspec etc. Nowadays only edge connectors are gold plated. Immersion plated gold is also used but it doesn't last the distance like gold plate
Electronics Forum | Fri Feb 28 00:42:40 EST 2020 | luciano_zhang
What is the use of gold plated boards?
Electronics Forum | Thu Nov 11 14:29:18 EST 2010 | davef
When you say 'tarnished,' is that based on: * Appearance of the gold over-plate * That you can't get good contact during ATE processing ... OR ... * Something else?
Electronics Forum | Fri May 03 16:06:44 EDT 2013 | hegemon
To be short, no change in profile is going to get you through this. As I recall the point of hard gold is to retard the wetting process, so no surprise here. For example a connector might have hard gold plating at the mating surface, but not at t
Electronics Forum | Fri Jul 16 22:44:27 EDT 1999 | Vic Lau
| We are currently assemblying several different board type with gold plated lands with varying results. Can any of you that has successful experience in this area give me some pointers. What paste do you use? Do you use the recommended reflow pro