Electronics Forum | Fri Feb 28 10:07:29 EST 2020 | stephendo
Flatness is only half of the advantage. Gold doesn't corrode. There are other flat surfaces but do not last as long as gold.
Electronics Forum | Tue Jun 28 09:13:46 EDT 2005 | russ
It appears that the reflow profile was incorrect or the paste was in bad shape on these boards from what I can see. I personally have never seen a board finish cause this symptom.
Electronics Forum | Tue Jun 28 10:41:57 EDT 2005 | GS
I am not an expert but just for my understanding: - solder paste used ? NC ? other ? - reflow in Air or N2 ? - temp ramp up before soack (�C/second) ? Tnks GS
Electronics Forum | Tue Jun 28 13:23:56 EDT 2005 | Bob Gilbert
Matt, Try a cooler profile by simply speeding up the conveyor by 10%. The difference may be the temperature the pads are reaching between the HASL boards and the Au boards. Are they the same thickness?
Electronics Forum | Tue Jun 28 17:38:13 EDT 2005 | mdang
We got the same problem. To solve it, we have to tint the pads first and do the normal reflow process. It works but take a lot of time to tint the pads. Any thoughts? Thanks, -Michael
Electronics Forum | Tue Jun 28 18:40:36 EDT 2005 | Bob Gilbert
Matt, Try putting a soldering iron to a pad to see if you get reflow. If it reflows, your oven is too cool. If no reflow, your oven may be too hot. Regards, Bob
Electronics Forum | Wed Jun 29 18:37:41 EDT 2005 | russ
I guess it's it's a good thing that they didn't work out. It might have been interesting when all of the boards failed down the road. I knew I should have asked if it was enig instead of assuming that it was.
Electronics Forum | Fri Jul 08 06:38:51 EDT 2005 | mattkehoe
I did not get that info. We sent them back and the vendor ran them through HASL finish. They processed very well after that. Thanks to everyone for the help. mk
Electronics Forum | Tue Jun 28 07:27:32 EDT 2005 | Matt Kehoe
We are experiencing a situation that we would really appreciate some expert opinions on. Our process prints solder paste then reflows it without components. Normally the paste wicks into a very shiny rounded meniscus. Even over gold, the round pads a
Electronics Forum | Tue Jul 11 12:59:26 EDT 2006 | mattkehoe@sipad.com
We are trying to apply solder to boards with 80 microinches of electro plated hard gold. No components involved, just print 63/37 paste and reflow. The results are very poor on some boards, not so bad on others? Pictures at http://www.sipad.net/thick