Electronics Forum | Fri Feb 28 01:36:43 EST 2020 | crystal12
> What is the use of gold plated boards? <BR> <BR> With the increasing integration of IC, the more IC the more dense. The vertical tin spray process is difficult to flatten the pads, which brings difficulty to the SMT mounting, and
Electronics Forum | Sun Apr 05 00:23:53 EDT 2020 | researchmfg
1. To protect the nickel and copper under gold plating from oxidization before soldering. Gold plating can extend the PCB self-life and improve the solderability for 2nd re-flow. 2. Provide a good bonding strength. For Chip on Board process that Gol
Electronics Forum | Thu Nov 10 12:29:57 EST 2022 | stephendo
The G in ENIG is gold. It does not oxidise. Either you are thinking of OSP or your board shop is providing defective boards if your boards show oxidation. It would be the nickel that is oxidising but should be totally covered by the gold. Is there
Electronics Forum | Thu Nov 10 20:39:44 EST 2022 | SMTA-64386598
The solderability shelf life of ENIG is related almost entirely to diffusion of O2 through the gold plating. When O2 diffuses through the gold, the underlying nickel is oxidized rendering it unsolderable (with ENIG - you solder to Ni, the gold dissol
Electronics Forum | Fri Jan 06 00:03:10 EST 2023 | SMTA-64419298
Hello Evtimov, sorry...just saw post as I was looking through list...a bit late. I don't know if you ever got your answer. IPC-4552A covers EniG finishes and suggested shelf life. I've referred to these doc's quite a bit. Good spec's ! Yes, I beli
Electronics Forum | Mon May 15 12:36:12 EDT 2017 | edhare
I don't believe there should be any issues with > the HASL finish. The issue is how long on the > shelf and is a bake out required to remove > moisture from PCB, as in any FR4 PCB's that may > have had time to absorb moisture. > I don't believe
Electronics Forum | Sun Jul 29 08:36:39 EDT 2001 | davef
You have provided very little information. Two similar possibilites come to mind: poor pad solderability protection and old boards. POOR SOLDERABILITY PROTECTION: Maybe the nickel plating under the gold is oxidized, contaminated, or otherwise very
Electronics Forum | Mon Feb 27 09:09:36 EST 2006 | davef
Silver on your copper or brass part is a solderability protection. The silver diffuses into the solder and you solder to the base metal, either the copper or brass in your case. Soldering to copper is well known. The issues are soldering to brass
Electronics Forum | Fri Nov 07 15:57:56 EST 2003 | Marc Simmel
Are there specifications or recommendations for electro-deposited tin-lead plating thickness on austenitic stainless steel that would provide a shelf life of 1 year? 6 months? Would 2 to 3 microns (78 to 118 micro-inches) 90/10 tin-lead over 1.27 mi
Electronics Forum | Sat Nov 08 10:04:26 EST 2003 | severs
Once you have selected your plating based on electrical and physical requirments, you should know that there is an inexpensive plastic storage packaging developed by Lucent which can keep any platings solderability from degrading for up to 10 years o