Electronics Forum | Mon May 27 11:13:11 EDT 2013 | ericrr
Is there any good articles to read on solder paste? (just to see if I may of missed something) Sometimes I can not believe the people I have to work with. We had a panel with two “Quad Flat Package” (QFP) one in each of the two circuits, almost fr
Electronics Forum | Fri Jun 25 15:48:55 EDT 2004 | tcp
The potting definitely is a factor in fracturing the grainy joints, but does not seem to damage a "good" solder joint.
Electronics Forum | Tue Apr 12 04:50:33 EDT 2005 | amstech
Nitrogen flow helps good joints. But proves to b expensive. Choice will be yours.
Electronics Forum | Sun Jul 05 12:47:44 EDT 1998 | Bruce Carnegie
What should a good gold joint look like? We've run boards for our customers that look kinda dull but seemed to wet properly and the boards fired up just nicely! Should they look nice and shiny like our HASL boards or is "a shiny joint is a good joint
Electronics Forum | Mon Jul 06 08:36:26 EDT 1998 | Steve Schrader
| What should a good gold joint look like? We've run boards for our customers that look kinda dull but seemed to wet properly and the boards fired up just nicely! Should they look nice and shiny like our HASL boards or is "a shiny joint is a good joi
Electronics Forum | Mon Jul 06 12:05:56 EDT 1998 | Srirama T. Reddy
| | What should a good gold joint look like? We've run boards for our customers that look kinda dull but seemed to wet properly and the boards fired up just nicely! Should they look nice and shiny like our HASL boards or is "a shiny joint is a good j
Electronics Forum | Mon May 31 05:55:22 EDT 2004 | johnwnz
Hey there, trying to get soem useful data on joints that suffer from gold embrittlement. Anyone got any data on effects ont he electrical conductivity of the joints over time? does it degrade quicker than a normal good joint? (let's all ignore the fa
Electronics Forum | Tue Jul 11 04:14:24 EDT 2006 | Rob
1) Use insulated wire & only strip back as much as you need for a good joint. 2) Wrap insulation tape around each joint (package lead with wire) after soldering to avoid any possibility of touching.
Electronics Forum | Mon Feb 15 15:43:06 EST 1999 | Dave Jurena
Hope some of you out there can help me with this one. I am getting feedback from our test department that they are showing opens on solder joints which have visually good wetting. The touch-up operators confirm that the joint looks good. All they do
Electronics Forum | Sun Jun 10 11:08:26 EDT 2001 | nifhail
I know that there is no pre-defined strength for the solder joint as it will depend on solder volume deposited, pad geometry, lead component's lead solderability etc. but, what would be the best ball park for the good joint for 0402, 0603, 20 mil pti