Electronics Forum | Mon Oct 22 15:41:39 EDT 2007 | davef
Bruno The real question about your troop using Kester 951 wave solder flux on boards is: how is the flux applied and controlled. See, when you apply this flux with your wave solder fluxer, it is ideally applied in a metered fashion with your fluxer
Electronics Forum | Mon Oct 22 11:47:59 EDT 2007 | brulal1
Thank you guys for your help, I do not clean any on my assemblies who are build by the SMT an wave soldering department, we do used liquid fluxes Kester 951 and cored wire keester 245, usually it�s for batteries connector, led, terminal and wire rap
Electronics Forum | Mon Mar 25 21:45:22 EDT 2024 | buckeye
I got an inquiry from one of our electronics labs with regards to their soldering processes. They use eutectic (63% Sn, 37% Pb) solder. For liquid flux they are currently using Kester 186, which is an old-school, full rosin (RMA and ROL1) flux that c
Electronics Forum | Wed Jul 28 11:47:16 EDT 2004 | GCronin
I am looking for a consistent method of applying no clean liquid flux to solder pads. My main concern is if I use a standard air-over type dispenser mounted to an automated arm that the liquid flux will make a mess and not be consistent. I'm not to
Electronics Forum | Sun May 30 18:52:35 EDT 1999 | Graham Naisbitt
| | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a
Electronics Forum | Mon May 31 15:09:56 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Mon May 31 15:10:14 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Thu Sep 06 10:55:37 EDT 2001 | davef
saturation occurs at ppm levels. Remember, IPA is extremely flammable and its bulk use makes the plant liable to all sorts of quite repressive safety rules/regulations and so on. Ignoring these rules exposes the owner to fines and possible plant cl
Electronics Forum | Fri Jan 15 03:30:10 EST 1999 | Jeff Sanchez
| Hi all, | | I thought I'd use this forum to ask a couple general questions on fluxes for manual operations: | First - Is it OK to use a wave soldering type flux (specifically OA)? Thinking about activation temperatures and the ramp rate of the wav
Electronics Forum | Tue Dec 17 14:11:43 EST 2019 | kylehunter
Haven't run those boards again, so haven't had the issue.. Since it seems like we may want to start using more aggressive flux based paste soon, what are some good choices? Ideally I'd like to stay with Kester, since they are readily available. EP2