Electronics Forum | Wed Feb 26 22:22:00 EST 2003 | Grant Petty
Hi, The guys here have some boards that have been reworked however as we use no-clean paste we are getting the white residue after ultrasonic cleaning. We are using an alcohol based cleaner in the ultra sonic cleaner. Does anyone have any ideas, or
Electronics Forum | Mon Jul 08 03:09:12 EDT 2002 | Benny
Hi all How can I find the technical paper or source of information about using No-clean flux with high frequency apllication. High frequency mean more than 2 GHz - 5 GHz. I heard from my colleague that No-clean flux residue on board effect to high
Electronics Forum | Mon Dec 13 16:25:37 EST 2004 | saragorcos
Hi Scott - No clean assemblies have a very low tolerance for processing residues, and long term reliability is compromised if residues from incoming bare boards, components, or un-solublized flux residues are not dealt with. It is critical to contro
Electronics Forum | Fri Oct 19 13:57:17 EDT 2007 | Michael Konrad
Hi Rob, I must take issue with your statement �By definition, no clean solder can be not-cleaned�. All no-clean fluxes can be cleaned. Whether or not one cleans no-clean depends on a variety of factors. More than eighty percent of all post reflow
Electronics Forum | Thu Jan 16 15:55:31 EST 2003 | MA/NY DDave
Hi I have a funny feeling that Mike Konrad and I know each other from IBM-Endicott days, yet I could be wrong. It would be funny?? Mike gave a good answer. The Rosin or Rosin Mildly Activated Flux (RMA) if on the board at ICT (In Circuit Test) wil
Electronics Forum | Mon Jul 01 00:09:47 EDT 2002 | Ben
Hi all How can I clean the white residue between QFP 0.5 mil Pitch? The white residue was created from mistake adding liquild No-clean flux Lonco 23F for reworking clean board. I can clean almost of it by using EC7M cleaning solvent except between
Electronics Forum | Tue May 21 00:24:34 EDT 2002 | ianchan
yngwie, Hi mate, and Holy Crap! what a blooming pile of 7 feet dung you have sitting on your front lawn! ok, we had a customer SQE like that before, fortunately she was promoted from SQE to purchasing officer. and in the name of universal sharing,
Electronics Forum | Fri Jan 21 13:57:52 EST 2005 | saragorcos
Hi esoderberg - I was wondering if you had tried altering your soldering profile to try and fully solublize the no clean flux residues and elimate your cleaning dilemma? You can check out my company's website if you want some free reference material
Electronics Forum | Tue Feb 24 18:04:22 EST 2004 | adlsmt
Im using Hi-Grade 1075 now. Is the 3541 a no-clean?
Electronics Forum | Wed Jan 17 10:01:49 EST 2007 | lyetc
Hi...have you try ultrasonic cleaning before rinsing?