Electronics Forum | Thu Oct 11 14:44:46 EDT 2007 | bbarton
Lots of papers out there on HiFreq circuits and the effects of solder paste residue. Google Dr. Karen Tellefsen. Simple test...take a "failed" board, remove the residues, test again. Has the problem gone away?
Electronics Forum | Mon Nov 05 19:43:09 EST 2007 | davef
"Effects of surface finish on high frequency signal loss using various substrate materials" - Call Don Cullen at Mac Dermid or Larry Gatewood at Rockwell Collins for a copy.
Electronics Forum | Sun Nov 04 05:11:14 EST 2007 | omidjuve
can you send me the articles about the high frequency boards issues with different types of solder paste alloy because i can`t find any free document about this article
Electronics Forum | Wed Oct 10 12:20:44 EDT 2007 | slthomas
Does it fail to function or does it function outside of acceptable tolerances? If the latter I wouldn't know what to think, but if the former I would feel obligated to suspect solder quality or maybe even a component problem with the elevated lead-
Electronics Forum | Wed Oct 10 12:04:54 EDT 2007 | russ
everything else EXACTLY the same? meaning exact same product number from the same manufacturer same fluxes used in the paste? no additional no clean "touchup" or hand soldering operations? No expert by any means but it would seem odd to me that the
Electronics Forum | Wed Oct 10 13:59:49 EDT 2007 | petep
I have always understood that on boards (or circuits) operating over 900 MHz, No Clean fluxes are to be avoided. Apparently the residues left behind, while non-conductive and non-corrosive, will change impedence of the circuit. It may be a possibil
Electronics Forum | Wed Oct 10 02:04:10 EDT 2007 | omidjuve
hi we use a no clean solder paste with the sn63pb37 alloy and our high frquency board doesn`t have any problem in test but after this product is finished now we use 2 different solder pastes 1. sn62 pb36 Ag.4 RA tape 2. NC type lead free with Ag i
Electronics Forum | Mon Jul 07 00:33:12 EDT 2003 | praveen
First we have to look in to the current situiation of the SMT line.Is the pick and place machine very old and can not perform consistently. Is the board to be inspected is very dense and have lots of connectors and fine pitch comp.with lots of 0402 c
Electronics Forum | Mon Jun 08 13:26:59 EDT 1998 | D.Hammond
I work QA at an OEM in Alberta, Canada. I saw earlier posts on the smtnet regarding PCB haloing criteria. I am currently in a dispute with my PCB vendor over the acceptability of haloing (delamination) around plated through holes and vias on a lot of
Electronics Forum | Fri Mar 24 17:07:39 EST 2000 | John Thorup
Hello Ashok If you are talking about the thousands of volts that is often generated by either simply unrolling the tape to apply or when it is removed from the board after soldering you don't have a lot of choice since it is an insulator. Ionization
COT specializes in high quality SMT nozzles and consumables for pick and place machines. We provide special engineering design service of custom nozzles for those unique and odd components.
2481 Hilton Drive
Gainesville, GA USA
Phone: (770) 538-0411
winsouce.jpg)