Electronics Forum | Tue Jul 27 12:45:34 EDT 2010 | kmtan
Hi expert, we have one lead frame product proposed to send to flux clean recently. The problem here is the frame is attached with high temp tape. After flux cleaning the frame, the tape turns out deformed in which we think it was due to chemical reac
Electronics Forum | Wed May 26 15:02:40 EDT 1999 | Paul Bonstrom (SGI)
Looking for help in finding suitable high temp gasket for use in smt assy support application. Gasket used to restrain flex on smt module in area prone to localized heating due to nearby device removal (hot air). Current gasket mtl (neoprene) degra
Electronics Forum | Wed Nov 20 10:50:49 EST 2002 | dphilbrick
Kester has a special alloy for high temp soldering. Alloy 123. I would think that if you coocked 63/37 to 360c you would have a pot of dross in no time! Doug
Electronics Forum | Wed Nov 20 07:50:00 EST 2002 | aerineng
Hi, I'm an SMT refugee working in component manufacture - hey, times are hard! I've been asked by a customer to test some of my parts at high temperature on the wave - up to 360 deg Celsius. I've checked my wave and it's only capable of getting up
Electronics Forum | Wed May 26 16:36:02 EDT 1999 | John Thorup
| Looking for help in finding suitable high temp gasket for | use in smt assy support application. | | Gasket used to restrain flex on smt module in area prone | to localized heating due to nearby device removal (hot air). | | Current gasket mtl (n
Electronics Forum | Tue Feb 17 15:24:17 EST 2009 | glynnhamer
I know this is going to sound rather sad, but we have been using a Capton tape for years that contains silicone to mask large components as they go over the wave, as well as large plated holes on the pcb. It was handed down for years as accepted prac
Electronics Forum | Wed Feb 18 22:18:26 EST 2009 | davef
"acrylic adhesive" "high temperature" tape
Electronics Forum | Wed Mar 16 20:12:12 EST 2005 | bkd
Does anyone knows any vendors that supplies jedec precondition tray that could stand up to 270�C peak reflow temperature.
Electronics Forum | Fri Sep 22 12:37:18 EDT 2000 | jonyoder
I am having problems with SMT electrolytic capacitors expanding and changing values after going through our reflow. The reflow profile we use includes temperatures of 200 deg C for 60 seconds and 230 deg C for 30 seconds. We need to use this profil
Electronics Forum | Wed Feb 15 15:27:35 EST 2006 | russ
Put this one out a little early! I just looked at the data in the Kic site and also at the other place, it is interesting how the results are different except for the high temp solder which we should have all expected. Now for my question Do we re
.gif)