Electronics Forum | Sat Jun 09 00:53:34 EDT 2001 | ianchan
Hi Folks, My Production runs a uBGA-liken product, and uses Pallets to support the 0.8mm thick pcb, during the SMT + reflow oven process. Process/QA see occurs: 1) 0402 unsolder? 2) 0402 tombstone? 3) "uBGA" poor-visual joints (dry joints)? Took
Electronics Forum | Wed Aug 06 14:49:06 EDT 2014 | dyoungquist
Sn62Pb36Ag2 has a higher liquidus point of 189C as compared to Sn63Pb37 at 183C. You may need to slightly adjust your oven profiles to use it compared to SnPb. We have had good solder-ability and reliability with it in our IPC Class II products. A
Electronics Forum | Wed Apr 14 12:23:59 EDT 2004 | Ted
Hi everyone! I am looking for a lead-free solder that will survive a customer reflow of 260C. I am currently using SN10/Pb88/Ag02 but the reflow temperature is to high (320C) for the FR4 boards that we have. I know there are higher temp FR4 boards
Electronics Forum | Mon Dec 30 23:37:47 EST 2019 | agoesfirmanto
Hello All, I am a SMT Engineer from Indonesia, I am facing the problem of soldering balls in only one IC location, in other areas there are none. solder ball defect almost 30%. I have done several actions but failed to reduce the solder ball. 1.
Electronics Forum | Wed Jul 27 09:58:05 EDT 2011 | davef
Pressure printing systems Conventional stencil printing techniques have fundamental limitations as regards paste handling: The volume of paste available for printing is limited, so frequent replenishment is necessary Paste is difficult to c
Electronics Forum | Thu May 11 11:25:56 EDT 2017 | davef
Key to Rosin Fluxes [from SUPERIOR FLUX & MFG. CO.] Type R (Rosin): Non-activated rosin flux for soldering copper. Residues are non-corrosive and non-conductive. Type RMA (Rosin Mildly Activated): Mildly activated rosin flux that contains no chlori
Electronics Forum | Thu Jul 28 09:47:06 EDT 2005 | fctassembly
Hello Carl, The main reason there is little information on lead free soldering to ENIG is because most of the lead free soldering to date has been Japanese consumer products. To keep costs down, the major surface coating used has been OSP copper. It
Electronics Forum | Wed Jan 27 11:58:35 EST 2010 | randyw
Our products are a mixed technology; with both surface mount components solder side and through-hole top side, in addition to massive heat sink assemblies. We have been using your SN100C solder in our wave solder process with Multicore MFR301 Flux si
Electronics Forum | Sat Nov 21 12:28:00 EST 2009 | flipit
There is evidence of lead being used in soldering 5000 years ago in Mesopotamia. Not a big issue for most people doing SMT but the poster should also understand why percent metal is adjusted for different solder paste alloys. You print by volume b
Electronics Forum | Wed Dec 06 07:24:22 EST 2006 | davef
Successful solder paste overprint is a function of the solder paste rheology, solder mask and through hole component stand off. * Solder mask with a high surface energy will permit a larger overprint than a solder mask with a lower surface energy. In
.gif)
winsouce.jpg)