Electronics Forum | Fri Jul 22 07:21:14 EDT 2005 | Mark
Try using Cobar`s anti-tombstone alloy.
Electronics Forum | Tue Jul 05 15:21:46 EDT 2005 | russ
So your thermal cycling test is putting these solder joints into reflow (183C + if they are lead joints)? Must be quite the test! Tell us what pad sizing and spacing you are currently using.
Electronics Forum | Tue Jul 05 13:54:35 EDT 2005 | Sandeep
We are facing lot of problems with tombstoning in 0201 components. Ironically tomstoning in these components is not occuring while reflow but it is happening when we subject them to thermal cycling test. We have been investigating the cause and thoug
Electronics Forum | Fri Jul 29 19:12:30 EDT 2005 | Jason Fullerton
In the true sense of the term, tombstoning can only occur during reflow. Now, if your solder joints are cracking during thermal cycling and opening on one end you still have a problem - it just isn't "tombstoning". What laminate are you using on yo
Electronics Forum | Sat Jun 13 07:22:13 EDT 1998 | Toni Casas i Pujadas
We are very concerned about outgassing in wavesoldering. If anyone knows how to use properly well pcb's before soldering in order to avoid this problem please let me know. I have this problem in FR4 large double sided pcb's. My soldering line is SOLT
Electronics Forum | Thu Nov 20 03:58:39 EST 2014 | hhat
To get the best performance of electronic circuits, components and circuit board supports circuit components and devices in electronic products. Even if the circuit principle diagram design is correct, the printed circuit board is designed improperly
Electronics Forum | Mon Jun 15 13:23:16 EDT 1998 | Bob Willis
| We are very concerned about outgassing in wavesoldering. | If anyone knows how to use properly well pcb's before soldering in order to avoid this problem please let me know. I have this problem in FR4 large double sided pcb's. My soldering line is
Electronics Forum | Sat Jun 13 11:00:21 EDT 1998 | Earl Moon
| We are very concerned about outgassing in wavesoldering. | If anyone knows how to use properly well pcb's before soldering in order to avoid this problem please let me know. I have this problem in FR4 large double sided pcb's. My soldering line is