Electronics Forum | Fri Mar 31 15:58:07 EDT 2017 | jutikagokarn
Thank you for your response. We build boards on an SMT line that is shared with other companies too and are currently using water soluble flux based solder paste on both boards. We realized an issue with washing on one of the boards so requested to
Electronics Forum | Fri Mar 31 13:59:21 EDT 2017 | westshoredesign
Need more information. BUT if your strictly considering just the paste change. I would imagine your changeover would be little to no different than changing to the second board if you were using the same paste. Maybe take extra care cleaning your sq
Electronics Forum | Thu Feb 27 02:55:53 EST 2020 | hexton
I want to avoid peoples preferences as they will differ and will not be a deciding factor. A heat gun will introduce risk to surrounding PTH components and having to add protection for those, will limit any gain in productivity. There is no question
Electronics Forum | Thu Sep 27 17:25:33 EDT 2007 | chef
The short answer is immediately after reflow the problem occurs. To be more exact, what you are describing is not "rust". Rust occurs in iron. The oxidation that occurs in Tin-Lead has been sometimes called "white rust". Either way, oxidation occur
Electronics Forum | Wed Nov 17 11:20:23 EST 1999 | Dave F
Hey Gyver: If you don�t mind (which you don�t have any choice about, because I�m going to do it anyhow, cause it�s MY word processor), I�m going to respond genericly, but still be directed to your question. Much of the following is paraphrased from
Electronics Forum | Wed Sep 27 13:45:35 EDT 2000 | Bill Schreiber
Dear Dreamsniper, A big hidden cost in any cleaning system is the cost of diminished production and rework. I assume you are cleaning the adhesive stencils manually since there is no equipment cost in your formula. Manual cleaning of adhesive sten
Electronics Forum | Wed Jul 04 12:35:19 EDT 2001 | davef
I thought I responded this this a while ago, guess NOT!!! Wow, Dano yagot Entek boards that are that old!!!! Coo. Sounds kwazy that you�d end-up with that volume of old boards, but it�s probably one of those deals where correcting the problem keep
Electronics Forum | Fri Dec 10 08:44:52 EST 1999 | Dave F
Vinesh: You�ll find no papers that "clearly describes the harmful effects" of your style "of white residues," because no one is crazy enough to brag that they are doing what your customer wants you to do. The residue of no-clean fluxes are designe
Electronics Forum | Tue Aug 27 08:13:29 EDT 2002 | mk
Our company uses a conveyorised aqueous cleaner to wash printed circuits after water soluble solder paste is reflowed. The system is closed loop with carbon and resin filters. The water eventually will get dirty. Can it be dumped? Treated? How do y
Electronics Forum | Thu Jan 28 08:58:10 EST 1999 | Peet
| | i am working with the noclean process and getting white residues on the bottomside of the board probably due to the | | wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated tempe