Electronics Forum | Thu May 18 19:45:32 EDT 2006 | grantp
Hi, The tin flush is a good idea, and better than the suppliers suggestion of filling with lead-free solder which is much more expensive. I guess we won't be leaving a KG of solder in the bath, but based on your experience, how much remaining sold
Electronics Forum | Mon Mar 27 15:56:12 EDT 2017 | padawanlinuxero
Just 2 cents, lead free flux residue is no clean?, how about leaded flux? how much flux residue it leaves on both types? is there a clean up procedure after wave solder? or is there a wave solder process?
Electronics Forum | Mon May 08 20:52:18 EDT 2000 | Dave F
Steve: A couple years ago, I decided that I needed to broaden my education in the areas(s) that I make my livelihood � soldering and assembly. I had attended some excellent (and some not so excellent) tutorials at NECON, but just felt I was missing
Electronics Forum | Wed Apr 28 17:27:31 EDT 1999 | Steve Gregory
Thank for the input. But I guess I was looking for more. We have been transferring boards for some time and a have good working relationship with our primary CEM and have worked out many bugs. I was thinking more on the order and don't shoot me bu
Electronics Forum | Wed May 24 17:49:51 EDT 2000 | Keith Luke
SMTneters, The end of May finds several recent publications from leading publishers on my desk. I am all too happy to share these books with our loyal SMTneters in the hopes that they will provide us with a timely review of the new release. For ma
Electronics Forum | Sat Jun 13 07:08:46 EDT 1998 | Dave F
| Is their an IPC standard for the water that is being used in the water wash. I have been looking and at this time have not found any thing. Steve: A lot of the old command and control specification environment has changed with the "industrializati
Electronics Forum | Tue Jan 08 10:10:29 EST 2008 | noid
We are building class 3 products, using no clean on wave and selective solder machines. Both processes are producing micro solder balls between the leads of through hole components. I have searched the site and haven't found any recent threads on h
Electronics Forum | Thu Mar 10 15:43:06 EST 2005 | steve
Thank you both for your assistance. I knew that I could count on you folks. The customer has purchased No-Clean flux and is using it as we speak. Hows that for customer service.... All in a days work... Thanks again You make me look good!!! Steve
Electronics Forum | Sat Jul 02 10:27:19 EDT 2022 | madisreivik
Hello ! I got exp only with leadfree HASL, but maybe the same problems apply. Also, the leaded HASL has probably lower process temperature. This could be copper, which has settled to the tank bottom. With leadfree, the copper is removed from molten
Electronics Forum | Tue Nov 25 05:20:20 EST 2014 | grimus
Could be. I am making overprint to achieve proper amount of solder paste inside hole. Now I am trying to reduce maximum overprint and compensate it with step - up stencil. This could reduce effect that some particles of solder paste are not gathering