Electronics Forum | Mon Jan 03 00:30:30 EST 2011 | raghu
Contact your distributor for the coating or > Humiseal directly. Humiseal has had a recent > issue with batches of 1B31. The specific problem > is lack of adhesion, which is what you have as > well. You need to find out if your batch # is one >
Electronics Forum | Tue Dec 20 10:10:21 EST 2005 | SteveH
Ours is the same configuration as that, we run with neat Humiseal 1B31 through the needle valve and a 1:1 blend 1B31/Butanone (MEK) in the spray valves. Programming is done via a PC using the pendant and the path is point to point trained on scrap P
Electronics Forum | Wed Feb 28 20:10:08 EST 2001 | mhunter
Checked the archives with no luck. Anyone have a reliable test method of verifying acrylic conformal coat cure. Using Humiseal 1B31 mixed with approximately 30% solvent, spraying with a Nordson. Thanks in advance.
Electronics Forum | Wed Feb 28 20:16:26 EST 2001 | mhunter
Checked the archives with no luck. Anyone have a reliable test method of verifying acrylic conformal coat cure. Using Humiseal 1B31 mixed with approximately 30% solvent, spraying with a Nordson. Thanks in advance.
Electronics Forum | Mon Aug 09 07:13:08 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problemsd
Electronics Forum | Tue Aug 10 01:02:31 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problems
Electronics Forum | Fri Nov 12 04:48:02 EST 2010 | raghu
thanks for your reply sir, for conformal coating Humiseal 1B31, what are the preferable staking materials? please suggest us..
Electronics Forum | Wed Nov 24 13:36:48 EST 2010 | diamondmt
I would suggest Zymet CN-1703 for staking of the components using this coating material we use it very extensively with Humiseal 1B31, if you would like; I would be happy to coat a couple of your samples for your evaluation.
Electronics Forum | Thu May 02 14:07:53 EDT 2013 | duso02
I would suggest lowering the viscosity even more. Humiseal even sells 1B31 pre-mixed specifically for spray machines and the highest they go is 65cps.
Electronics Forum | Thu Aug 12 13:18:43 EDT 2021 | conro
The HumiSeal 1B31 is actually pretty fast drying e.g. 24h @ room temperature or 30min @ 76 °C Link