Electronics Forum | Fri Jul 24 16:37:47 EDT 2015 | cnotebaert
to my knowledge it will always be manual insertion,, if you mean reflow, not insertion, I always apply solder to one side, reflow, then apply tacky flux pre print to the already soldered pins, print op side, assemble part then send through placement
Electronics Forum | Thu Aug 09 15:16:20 EDT 2001 | Adam
Thank you Michael, yes we use a Fine Focus X-Ray machine, we also had some dummy connectors to play with, so we profiled the board until we reached a desirable profile. For placement we used a GSM machine, the only issue we ran into there is the par
Electronics Forum | Thu Aug 09 15:16:31 EDT 2001 | Adam
Thank you Michael, yes we use a Fine Focus X-Ray machine, we also had some dummy connectors to play with, so we profiled the board until we reached a desirable profile. For placement we used a GSM machine, the only issue we ran into there is the par
Electronics Forum | Wed Aug 08 09:47:00 EDT 2001 | Adam
I'm trying to develop a process for a small assembly consisting of two mirror image PBGA connectors, I've built the first prototype, but I ran into different problems: 1. The SMT connector was shifting during placemnt, and I knew one issue i have to
Electronics Forum | Thu Aug 19 05:12:41 EDT 2004 | bernardmulcahy
Hi Russ, Thanks for the reply -- It is not a double sided board so I guess I will be doing pretty much the same process as you described. I was wondering about was the tool you mentioned -- Is this just a fixture you got made locally or some specific
Electronics Forum | Tue Dec 11 11:59:00 EST 2012 | sarason
The issue is surface tension around the connector. Your tip needs to have more surface tension than the pins of the connector as it forms a cluster when being soldered. When I used to solder superfine connectors with a metcal iron it had a horses hoa
Electronics Forum | Wed Dec 29 14:30:28 EST 1999 | Dan Woodward
I am not sure if I have seen an article comparing solder joint strength Vs pressfit although I am sure this has been researched by literally hundreds of companies before they felt comfortable going to pressfit. I know one of the issues with solder is
Electronics Forum | Sat Aug 11 05:29:31 EDT 2007 | johnz
We are having a problem with JST connector ICM-MA50H-SS52-1161 LF SN. After reflow oven soldering we have mostly problem with soldering quality for firs or last leg of the connector. (There is no connection- leg just lays-lift on the solder no wicki
Electronics Forum | Tue Aug 24 21:52:06 EDT 2004 | rose
recently I met one very interesting issue with my board and connector. substrate of the board is copper with immersion silver, pad size is about 3x1mm. we print lead-free paste on the pad, then put the connector on the paste. The board was reflowed u
Electronics Forum | Wed Aug 25 20:48:17 EDT 2004 | rose
Hello recently I met one very interesting issue with my board and connector. substrate of the board is copper with immersion silver, pad size is about 3x1mm. we print lead-free paste on the pad, then put the connector on the paste. The board was refl