Electronics Forum | Tue Aug 22 10:06:53 EDT 2000 | George English
Has there been a definite date for the total move over to lead free? Will it be 2004 or 2008. Also is there a direct replacement for leaded solder, I have read various articles on numerous alloys suggested for the switch, such as bismuth, tin, copper
Electronics Forum | Wed Jan 03 21:20:22 EST 2007 | davef
Comments are: * General purpose RTV (RTV-108) releases an acetic acid (vinegar) during cure and corrodes copper, brass and sensitive metals. It is therefore NOT for use in delicate electrical or electronic applications. However, there is an electrica
Electronics Forum | Mon Mar 26 16:58:53 EDT 2018 | solderingpro
Is there anything stopping you from replacing the flat belt solution to a continuous running steel roller chain conveyor? - From there (depending upon board temperature) you should be able to buffer your boards in a vertical buffer station if neede
Electronics Forum | Mon Mar 03 13:18:02 EST 2003 | msivigny
Hello phil, The use of AOI systems give us the opportunity to auto-collect defect information much the way you're using them now. AOI systems become extremely effective when the collected data is used to perform some positive change into the process.
Electronics Forum | Wed Mar 05 12:23:31 EST 2003 | msivigny
Hello Phil, We did use an Oracle relational database with an Access front end to input and query data from the system for reports. We did not perform SPC with the Oracle dB. As the whole data collection process was completely customized, we hadn't im
Electronics Forum | Mon Jul 28 11:31:42 EDT 2008 | blnorman
Ideal situation is get a technical rep from the solder paste supplier. They know their paste better, and should be able to work out a profile based on their paste and your oven. Again, a technical rep, not the sales guy.
Electronics Forum | Wed Dec 22 08:49:55 EST 2004 | markhoch
I'm looking for some data to support my argument that HASL boards are not the most ideal boards for manufacturing involving BGA's and 0402's. I'm sure one of you SMT Gurus out there can point me in the right direction! Thank you in advance!
Electronics Forum | Thu May 25 01:46:10 EDT 2023 | frankchan
Hi, I would recommend something from 21 Century at least. Considering it's mostly small batches there's no reason to raise the budget to purchase the Newest series. I think the principle here is something that'll do and do a nice job. If you are a Ya
Electronics Forum | Mon Oct 19 15:43:37 EDT 2009 | dilogic
We have a problem with QFN IC's with NiPdAu plated pads. Our ULC's don't see the pads due to the almost ideal reflection. Vision sees the pads almost black. As we don't have OAL-cameras (which can help in this case, I assume), I am thinking of back-l
Electronics Forum | Thu Apr 21 11:43:03 EDT 2005 | davef
We understand the problem of trying to coat over RTV. We have seen the same problem with acrylic and urethane coatings not wanting to stick to RTV. Some acrylics seem to be worse than urethane. Since this is a new product, may be you could pot your