Electronics Forum | Wed Sep 03 07:43:13 EDT 2008 | davef
What do you mean by a "few micron thick"? IMC thickness pre-cycling (NEMI Lead-free) * Cu3Sn: 3um [118 uin] * Cu6Sn5: 1um [40 uin]
Electronics Forum | Wed Sep 03 16:59:13 EDT 2008 | glennster
At a former employer we required HASL thicknes to be a minimum of 0.75 micron (30 microinches), as measured at the thinnest point on any given pad. This would generally assure a minimum 1 year solderability shelf life. Usually when we saw a soldera
Electronics Forum | Wed Oct 24 18:08:02 EDT 2001 | davef
1- DF1: WOW!!! How do people get these cool toys? CB: I am with the University at Buffalo Electronic Packaging Lab. http://www.packaging.buffalo.edu We have pretty much everything that is sold on the market as well as Laser inspection technologies we
Electronics Forum | Thu Dec 07 17:25:58 EST 2017 | davef
Help me understand your issue better ... Are you looking to: * Improve your products that are used for thermal cycling testing of products of other companies? * Change your production materials so that you pass thermal cycling testing of your produ
Electronics Forum | Mon May 20 21:29:52 EDT 2002 | davef
Q1: Are we saying then that IMC can occur at the solder / Cu pad join on the PCB when finished assembled? A1: Yes, but in a broader context I am saying that when someone solders correctly, they form an IMC. Q2: Will the tin diffuse with the Cu over