Electronics Forum | Tue Aug 20 18:15:02 EDT 2002 | davef
Haaaaa!!!! Soldering to plastic!!!! An apt analogy!!! I like to compare it to soldering to dirt. Some thing. In fact, you are soldering on nickel, when soldering on many things. It�s just that the gold, er Pd, flash enables the wetting mechanism
Electronics Forum | Tue Mar 14 16:26:45 EST 2006 | patrickbruneel
BeCu is not solderable without plating Cu, Sn, Ag, Ni etc. The solder joint will only be as strong as the bond strength of the solderable plating to the BeCu Pat
Electronics Forum | Fri Apr 16 08:20:58 EDT 2004 | Bob L.
We've seen problems with BGA balls breaking at in-circuit test. I did some bend testing and found that our large BGA's can handle amazing stresses at low strain rates but we get brittle fractures at high strain rates, especially with Ni/Au surface f
Electronics Forum | Tue Jan 10 14:44:42 EST 2006 | greg york
Not sure about Sn/Cu/Ni large market share here in Europe as we have a large part of the UK market with SACP0307 alloy 0.3%Ag introduced over Two years ago Also worked against Sn/Cu/Ni alloy with large TV Co and they went with 0.3%Ag due to reliabili
Electronics Forum | Thu Sep 02 14:26:22 EDT 2004 | frankracine
Thanks Russ, very interesting. Are you working with a printer, PNP, reflow and wave? Did you change apertures in your stencils with lead free ? Concerning reflow, do you have a 5 zones, 7 zones ... ? Are you using the same alloys for solder paste
Electronics Forum | Tue Nov 05 09:57:45 EST 2013 | cuperpeter
Hello All, We have a problem with dewetting of solder paste. Problem is most visible on the pads without components (see attached pictures) and occurs randomly, 20% of PCB's. Pcb supplier sent us a cross-section of pads with thickness of Cu, Ni and
Electronics Forum | Tue Dec 01 09:02:18 EST 1998 | Earl Moon
| | | Hi folks , | | | Lately we are seeing a lot of rawcards with black spots on the pads - most of them have Au finish(immersion gold) . We did a lot of inspecton after wave solder and found that only (fine pitch) QFP are affected the most. Our in
Electronics Forum | Fri Dec 04 20:26:34 EST 1998 | kallol Chakraborty
| | | | Hi folks , | | | | Lately we are seeing a lot of rawcards with black spots on the pads - most of them have Au finish(immersion gold) . We did a lot of inspecton after wave solder and found that only (fine pitch) QFP are affected the most. Ou
Electronics Forum | Fri Dec 04 20:37:45 EST 1998 | kallol chakraborty
| | | | | Hi folks , | | | | | Lately we are seeing a lot of rawcards with black spots on the pads - most of them have Au finish(immersion gold) . We did a lot of inspecton after wave solder and found that only (fine pitch) QFP are affected the most
Electronics Forum | Wed Dec 13 10:24:52 EST 2000 | Wolfgang Busko
Hi Jack, I once tried this finish ( without changing any process parameters ) and encountered wetting problems even in the first reflow process. It was thought as cheaper alternative to Ni/Au we use for planarity reasons. Heard of the same problems