Electronics Forum | Thu Mar 24 07:06:06 EST 2005 | davef
There's a lot of comparison tables on the web. Here's one: Properties - Summary [A Winlow Circatex] Attribute||Hasl||Immersion Silver||Immersion Tin||Electroless Pd||OSP||Eless Ni / Imm Au Shelf Life (months)||12||12||12||12||12||6 Multiple Reflows
Electronics Forum | Thu Aug 31 12:17:56 EDT 2000 | mike weekes
We are considering alternative Board Finishes to our existing HASL process. The HASL effects opens on 25 and 20 mil packages after reflow and we know if the advantages of CuOSP and other alternatives. OUR Concern: Is there a shelf life and handlin
Electronics Forum | Thu Sep 02 10:24:35 EDT 2004 | dj_jago
Greetings from the UK: I have been quite fortunate to lead (no pun intended) our company towards lead free sooner rater than later. One of our customers produces a product which is refurbushed every 6 months or so and sent back into the market. A
Electronics Forum | Mon May 13 11:17:57 EDT 2002 | genny
I think for our company, the reason we have not yet tried it is two fold. One - we are just barely starting to see a need on a new product under design for a flat finish, so currently we don't use any of the really flat finishes available. Two - Silv
Electronics Forum | Thu Aug 31 18:59:55 EDT 2000 | Brian W.
Our customers use OSP, HASL, immersion tin and immersion gold as board finishes. If I recommend a finish to the customer, it is one of the immersion finishes or OSP. Those finishes have the advantage of a flat surface to deposit paste. HASL has va
Electronics Forum | Wed Dec 15 21:29:34 EST 2004 | davef
We�d say that it�s incorrect that ENIG solderability protection cannot be steam aged. It�s true the immersion tin and silver cannot be steam aged. We believe that most of the issues surrounding the poor performance of ENIG after steam aging is attr
Electronics Forum | Mon Dec 06 03:54:57 EST 1999 | Chris May
Hi Russ, I have a similar situation. I have been told that this can be caused by the nickel, over which the gold is plated, can result in suspect joints, embrittlement etc. Some joints can even be weak and broken without much force on some of my boa
Electronics Forum | Tue Jun 02 17:45:46 EDT 2009 | boardhouse
Hi Nicoleta, As a board shop, either are good choices but in my experience with my customers ENIG has alway been the favorite due to it is easier to work with in regards to not having to tweak your equipment. As long as the board shop that you are u
Electronics Forum | Fri Jul 09 18:36:48 EDT 2010 | rway
We don't use flex pcbs but have the same issue here. Most of our pcbs are HASL finish. I have looked at silver and gold immersion and both look really good under my color camera on my AOI. However, gold is more pricey. There is no additional cost
Electronics Forum | Tue Jul 15 16:12:23 EDT 2008 | boardhouse
Hi Armynski, I sell for an offshore board house, yes, it is common for offshore board shops to fill vias. The bubble is caused by air entrampment within the hole it self, when heat is applied during Hot air and the via is covered on both sides the e