Electronics Forum | Mon Aug 07 09:04:09 EDT 2006 | molos21
Hi everyone, I am starting to use the lead free process and I had a few wetting problems (solder did not reach top side) at the wave soldering process once the pcb had passed our smt line (one heat pass). From what I understand, I have had a problem
Electronics Forum | Sat Jul 28 08:37:52 EDT 2007 | davef
There is no good choice. Board Finishes: Industrial/Battelle Class 3 Environment [Reliability Knowledge Gaps: For use of Pb-free solders in High Reliability Applications, J Smetana, iNEMI Availability of SnPb-Compatible BGAs Workshop, March 1, 2007,
Electronics Forum | Tue Mar 01 10:21:55 EST 2005 | davef
IPC Plating Committee is presently working on a specification for immersion tin [IPC-4554 Specification for Immersion Tin Plating for Printed Circuit Boards] as a solderable surface finish. Immersion tin is normally deposited at 30 to 60 microinches.
Electronics Forum | Fri Apr 15 08:42:23 EDT 2022 | sn
Thank you for sharing the helpful information. Let's say the PCB is a double-side assemble process and this PCB has completed the first reflowing SMT assembly process, is there any concern if the board is kept on the production floor with temperatur
Electronics Forum | Thu Apr 14 06:02:59 EDT 2022 | sn
Hello! Anyone here knows is there any specific time frame (production time control) defined for a PCB assembly process completed SMT? How long need to complete the SMT process if double-sided SMD boards are assembled?
Electronics Forum | Sat Mar 05 22:44:44 EST 2005 | gpaelmo
You can also try the Florida Circtech website or call them direct. There is a min. thickness requirement and if the board house does not follow it you will end up with scrap boards after the second pass (from experience). I even sent blank boards to
Electronics Forum | Thu Aug 03 10:53:23 EDT 2000 | Roni Haviv
Hello, Does enyone have any experience with Immersion Tin (Sn) as a finish process on PCB ? Any information will help ! Thanks Roni
Electronics Forum | Wed Dec 24 15:28:17 EST 2008 | edmentzer
We use SN100C for wave soldering and hand Lead free soldering and have had very good results. The wire cored solder for hand soldering flows good and makes very good solder joints. The SN100C in the wave solder machine also works very good. We use
Electronics Forum | Fri Dec 16 08:00:26 EST 2005 | jax
What you are most likely dealing with: Insufficient Pure Sn layer ( multiple causes ) Because elevated temperatures accelerate the diffusion process, the thickness of the Pure Sn layer will reduce during every thermal cycle... ( bakeing PCBs, S
Electronics Forum | Thu Aug 03 12:44:07 EDT 2017 | davef
Try: * RD Chemical [ http://rdchem.com/chemposit-sn-rd-51.html ] * MacDermid [ http://electronics.macdermidenthone.com/products-and-applications/printed-circuit-board/final-finishes/immersion-tin/ ] * Technic [ https://www.technic.com/applications
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830