Electronics Forum | Wed Aug 09 08:06:07 EDT 2006 | davef
See "IPC-4554 Specification for Immersion Tin Plating for Printed Circuit Boards" 3.2.1 Immersion Tin Thickness. The most common reason for solderability issues with the white tin surface coating during multiple thermal excursions is a thin white ti
Electronics Forum | Mon Aug 07 09:04:09 EDT 2006 | molos21
Hi everyone, I am starting to use the lead free process and I had a few wetting problems (solder did not reach top side) at the wave soldering process once the pcb had passed our smt line (one heat pass). From what I understand, I have had a problem
Electronics Forum | Mon Oct 06 09:55:35 EDT 2003 | davef
While you are waiting for others to reply, search the fine SMTnet Archives on: * immersion and tin * imm and tin
Electronics Forum | Sun Oct 05 06:37:41 EDT 2003 | christ
Hi all: I want to know the parameter and criterion about the process of immersion tin,could you be kindly to give me the hins about it in more detail.Thank you for your support. Best wishes christ
Electronics Forum | Wed Jul 29 13:44:45 EDT 1998 | David Spilker
We are investigating alternatives to HASL finishes for more dense PWBs. OSP is not a good choice because of low solid flux and possibly long shelf life. Immersion gold is expensive and so far has been more difficult to wave solder. Has anyone had
Electronics Forum | Wed Oct 08 06:55:36 EDT 2003 | christ
Hi Dave: Thanking in advance for your valuable response!
Electronics Forum | Mon Aug 03 12:18:42 EDT 1998 | John Sikes
We have mixed to negative feelings about Omikron, but I beileve it is due to problems with the board fabricator rather than the process itself. When done properly, our Omikron boards have had very good solderability. However, we have had several ru
Electronics Forum | Wed Aug 05 07:46:46 EDT 1998 | Earl Moon
| We have mixed to negative feelings about Omikron, but I beileve it is due to problems with the board fabricator rather than the process itself. When done properly, our Omikron boards have had very good solderability. However, we have had several
Electronics Forum | Mon Nov 25 15:55:32 EST 2002 | davef
Sorry, no tricks for you. The good news is: your reflow recipe should be similar for both imm tin and HASL. Imm tin requires more attention to detail by both the fabricator and the assembler than HASL. There is a fair amount of discussion on imm
Electronics Forum | Mon Nov 25 09:06:15 EST 2002 | jax
You might want to check the tin thickness. I believe you have a minimum of .65 microns in order to achieve a good solder joint through 3 thermal passes. In an immersion tin process, the ability to solder is time and temperature dependant. As the int
.gif)