Electronics Forum | Wed Nov 16 21:35:07 EST 2022 | stephendo
" so I wander what can I do to save them?" The boards or management? Seriously I think this is more of a management issue than a technical issue. We can suggest what to do but if management does not accept that solution then it won't work. I'm not s
Electronics Forum | Tue Mar 20 09:03:18 EST 2001 | moseschee
Hi, I'm looking for research/study done on solder shelf life by using accelerated aging process ( steam age or dry air oven bake at 150C & etc ) Perhaps you could help to advise correlation of all this acceleration test to actual solder shelf life
Electronics Forum | Fri Aug 08 14:21:10 EDT 2003 | bman
Hello all, I'm working at a CM with less then ideal material storage shelving when it comes to ESD protection. I've got ordinary painted shelving units that I need make ESD safe. I'm considering dissipative mats or spray coatings for each shelf, t
Electronics Forum | Fri Aug 08 15:30:50 EDT 2003 | bman
Hello all, I'm working at a CM with less then ideal material storage shelving when it comes to ESD protection. I've got ordinary painted shelving units that I need make ESD safe. I'm considering dissipative mats or spray coatings for each shelf, t
Electronics Forum | Thu Jan 21 17:07:16 EST 1999 | ed zamborsky
I've had alot of success with the solder pastes from ESP in Rhode Island. They have great shelf life and are easy to print | I'm currently planning to do an evaluation of RMA flux solder pastes for mil type applications. Does anyone have any suggest
Electronics Forum | Mon Feb 23 13:21:03 EST 1998 | Gary Simbulan
Gary, Paladium Leads have been a win-lose proposition as far as I can tell. The vendors win because they don't have to deal with lead and get higher yields. The users lose because of extra engineering time involved with incorporating this on their
Electronics Forum | Mon Jun 14 11:44:23 EDT 2004 | Dreamsniper
I have boards with bad HASL application. First they're not even. Second some pad edges have no HASL and still remains bare copper. What's the maximum and minimum HASL thickness required for a good solderability. My boards are about 6 weeks old, I kno
Electronics Forum | Mon Jun 25 09:08:22 EDT 2001 | Dave G
What type of board finish ? I've seen this same defect with QFP's on some of our HASL boards. Best I can tell either the PCB's have poor solderability or uneven pad heights due to poor solder leveling at the PCB fab. Newer PCB's seem to yield bette
Electronics Forum | Mon Aug 28 17:04:52 EDT 2006 | Board House
ImSn - Immersion Tin - Not Recomended- short shelf life ImAg - Immersion Silver - Prefered Surface finsh by most Board houses, Best reworkablility, 12 moth self life, ENIG - Electroless Nickel Immersion Gold - Second Choice for Board Shops, 12 -
Electronics Forum | Mon Apr 16 18:49:40 EDT 2012 | tris101
Hi guys, I'm looking for some tooling parts and I hope you can point me in the right direction. We design basic in house reflow Carriers to surport boards during reflow. I would like to add clamps to our designs but I can not locate any off the she