Electronics Forum | Wed Aug 21 09:09:50 EDT 2013 | wcheew
I am having solder barrel fill issues on THM component, we follow, we follow IPC 610 E requirement. The barrel fill issues happen on signal & ground pin at connector & E-cap. I found out that most of the insufficient solder happen on the connector ag
Electronics Forum | Wed Aug 04 17:16:13 EDT 2004 | Richard
Can anyone comment on inspection criteria for PIH applications. I'm of the opinion that the inspection criteria used for wave soldered joints should be used for PIH. Some colleagues believe that a bottom side fillet is not necessary since the solde
Electronics Forum | Wed Apr 13 21:17:18 EDT 2022 | stephendo
If it was ROHS, I would say that the pads are definitely dissolved away. And it sounds like that is the case here. Your best bet is if it is class 2 and the barrels are at least 50% then push for them to be accepted. If you are trying for more barr
Electronics Forum | Fri Feb 21 19:41:25 EST 2003 | neil
I have had a look at what Bob Willis say's and the answer to my problem is not there. The paste we are using has a very high viscosity and I beleive that if we reduce the metal content to less than 90% it will solve the problem. The problem is parti
Electronics Forum | Fri Apr 04 09:54:39 EDT 2008 | redtiger56
We have been seeing continued difficulty with solder shorts and/or insufficient barrel fill with our Juki selective solder machine while using SAC305. We want to switch to something in the SN100 series, but we do not know enough to seperate the hype
Electronics Forum | Thu Aug 11 21:43:19 EDT 2005 | Ken
Those temp stickers are useless unless you can stick them into the copper barrel. They can only determine "skin" temperature which has nothing to do with what is happening in the barrels. Your solder is filling the barrel then going cold. I'll gua
Electronics Forum | Thu Apr 14 13:49:34 EDT 2022 | winston_one
Thank you for reply, Stephen. No, As I wrote it was leaded process. I heard that it is possible with lead free solder at higher temps an dwell time. At NPL Defect Database I've find this case wich looks exactly the same: http://defectsdatabase.npl.co
Electronics Forum | Fri Jun 04 03:03:52 EDT 1999 | Scott B
| I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." The
Electronics Forum | Thu Sep 30 12:29:01 EDT 1999 | Dave F
| Hi everyone, | | Greetings! | | I�ve got a 2-layered through-hole PCB�s having the following problems: | | Solder Mask peels after wave soldering at random locations and only at the bootom side of the PCB | Insufficient Solder and some solder ne
Electronics Forum | Thu Sep 30 21:37:44 EDT 1999 | Dreamsniper
| | Hi everyone, | | | | Greetings! | | | | I�ve got a 2-layered through-hole PCB�s having the following problems: | | | | Solder Mask peels after wave soldering at random locations and only at the bootom side of the PCB | | Insufficient Solder an