Electronics Forum | Mon Feb 26 20:02:42 EST 2001 | davef
First, I don�t understand why your board fabricator can�t do a good job plugging your vias. Additionally, when you consider that they forgot to plug the first batch of boards, it makes me wonder if they are desirable as a supplier. Generally, we us
Electronics Forum | Fri Apr 29 14:16:16 EDT 2011 | ppcbs
Below is the long explanation. This defect is most commonly found with BGA components, but can arrise with all components. I see it happening more now with lead free boards that are being assembled with a no clean flux. Best short term remedy is t
Electronics Forum | Tue Sep 25 12:50:13 EDT 2001 | mparker
Since you are mostly concerned about the flux and suspect an application issue, you need to do a few things to validate whats going on. 1. Forget about speed of processing, length of time to do the job. Focus on accuracy first, then speed. with that
Electronics Forum | Thu Apr 27 21:04:33 EDT 2000 | Dave F
Ron: Good news: Nicolet makes excellent machines. Bad news: I�m unaware of a machine with the capabilities you seek. * X-ray machines lack of resolution needed in relation to the crack geometries encountered within a high density single material.
Electronics Forum | Thu Sep 30 12:29:01 EDT 1999 | Dave F
| Hi everyone, | | Greetings! | | I�ve got a 2-layered through-hole PCB�s having the following problems: | | Solder Mask peels after wave soldering at random locations and only at the bootom side of the PCB | Insufficient Solder and some solder ne
Electronics Forum | Thu Sep 30 21:37:44 EDT 1999 | Dreamsniper
| | Hi everyone, | | | | Greetings! | | | | I�ve got a 2-layered through-hole PCB�s having the following problems: | | | | Solder Mask peels after wave soldering at random locations and only at the bootom side of the PCB | | Insufficient Solder an
Electronics Forum | Fri Oct 18 17:47:37 EDT 2002 | russ
What is the determination of poor soldering fails pull test, non-wetting, visual)? I have never heard of an SMT component that has leads higher than the body of the component. Refer to IPC 782 3.6.1.7 it provide the guidelines for SMT standoff heig
Electronics Forum | Tue Jun 08 11:40:03 EDT 1999 | Steve Skinner
| | | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VI
Electronics Forum | Fri Jun 04 10:02:06 EDT 1999 | Chrys Shea
| | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole
Electronics Forum | Fri Jun 04 17:10:59 EDT 1999 | C.K.
| | | I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | | | | | We've been getting a rash of defects that we call in this company, "insufficient solder in VI