1- DF1: WOW!!! How do people get these cool toys? CB: I am with the University at Buffalo Electronic Packaging Lab. http://www.packaging.buffalo.edu We have pretty much everything that is sold on the market as well as Laser inspection technologies we
Electronics Forum | Sat Sep 18 04:42:52 EDT 1999 | Brian
Dave, I'll respond by paragraph: | | | Brian: | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slathered shiitake burritos through
Electronics Forum | Sat Sep 18 12:27:21 EDT 1999 | Earl Moon
| | | Dave, I'll respond by paragraph: | | | | | Brian: | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slathered shiitake
Electronics Forum | Thu Jun 17 21:31:06 EDT 1999 | Dave F
| | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | for example: | | | | Solder Bridge | | 1.verify amount of flux been aplied. | | 2.verify turbulance on your solder w
Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Wed May 12 10:29:25 EDT 1999 | Timothy O'Neill
| | | Can anyone tell me what the recommended "typical" cooling rates are after reflow? Are the cooling rates considered as critical to control as the heating rates and why/why not? | | | I do not think there is a "typical" post reflow cooling rate
Electronics Forum | Tue Dec 08 17:55:51 EST 1998 | Dave F
1. What is the best way to remove polyurethane conformal coating from selected areas? Your conformal coat material supplier is best equipped to tell you how to remove the coating. Polyurethane conformal coating is not easy to remove. Without in-pu
Electronics Forum | Fri Feb 11 18:09:11 EST 2000 | Glenn Robertson
Russ - I agree with the other guys that the problem could be black pad or some intermetallic problem, possibly related to the "conversion" to HASL finish. But my first guess is still partial reflow at wave soldering. You won't catch it by push
Electronics Forum | Sat Nov 25 18:45:19 EST 2000 | Ashok Dhawan
I am getting black spots / stuff while I run gold finish PCB through reflow soldering process using NC solder paste.The affected spots have intermetalic as black in color. Does not solder very well. I did look at the archieve but could not find info
Electronics Forum | Fri Sep 22 05:33:59 EDT 2000 | Wolfgang Busko
That "C - it doesn�t matter" choice sounds good because it doesn�t give you a headache when profiling but it gives me a headache when I read the article in the current "newsletter" about profiling where I found this: "If soldering to gold over nick