Electronics Forum | Wed Aug 10 07:55:21 EDT 2005 | ajaydoshi
we are using heareous F381, F352 no clean solder paste. specially in qfp for high frequency board we observe that cleaing / removing of ' no clean flux 'is require. if we do not clean same most of time after all test & envioumental test it shows pin
Electronics Forum | Fri Oct 19 11:51:25 EDT 2007 | rgduval
By definition, no clean solder can be not-cleaned. The solder/flux are formulated to result in low ionic-contamination, hence, no cleaning. I have, however, always had at least one customer that requests their no-clean solder get cleaned. No-clean
Electronics Forum | Wed Jun 16 08:56:34 EDT 1999 | Vic Lau
Do anyone have any experience on assembling high frequency product, 1.8GHz or 2.4GHz. In our production line, we manufacture 1.8GHz product with using no clean paste (RMA type) for reflow and no clean wire for rework. In our functinal test,either a
Electronics Forum | Wed Aug 30 23:45:28 EDT 2000 | Ramon I Garcia C
Hi friends; Steve I'm using flux Kester 959, my top temperature is 187 celcius degrees, my e-mail is ramigary@smtnet.com, Travis I'll check the pcb for contamination, but how may I clean the pcb? may I use alcohol? Nance I cleaned the pipes of the
Electronics Forum | Sat Mar 27 12:36:34 EST 1999 | Scott Cook
| Hi, | I have a customer who's electronic assemblies produce RF. He is insisting upon aqueuos cleaning. We switched to a no clean solder years ago and no longer have an aqueous system. | Is aqueous cleaning necessary to eliminate 'cross talk' of
Electronics Forum | Mon Mar 17 04:31:52 EDT 2008 | d0min0
Hello, tried searching the SMTnet archives, but not yet a clear answer - maybe there is not a one yet ? ;) last discussion I found is few years old so maybe there is a fresh view on that? Q: we want to prove that our proces is "clean" we use SAC30
Electronics Forum | Wed Dec 05 18:19:39 EST 2012 | cnotebaert
You should talk to your paste/flux manufacture! They will provide the best instruction for this. The norm is typically 130-145f, speed 2-4f/m I always push for slower… the slower the cleaner/drier (in theory!), if you have an ICOM, Omega meter, ionog
Electronics Forum | Sun Feb 01 18:24:52 EST 2004 | Dean
Ok, maybe I'm missing something here: It's a no clean flux type AND your going to wash it? Why not migrate to OA Flux and just run DI water with Ion-Exchange beds? Benefits: No need for ultrasonics No need for chemical isolation No need for cleani
Electronics Forum | Mon Apr 22 16:55:42 EDT 2002 | russ
Greetings All, Anybody out there experiencing white residues after cleaning? We currently use a batch cleaner to clean water soluble fluxes. this cleaner makes its own DI water by means of carbon and resin tanks. After cleaning there are residues
Electronics Forum | Sun Feb 26 21:48:28 EST 2006 | Mike Konrad
Hi GS, Just a clarification� No-clean does NOT equal no ions. It equals less ions (at best). Automatic R.O.S.E (Resistivity Of Solvent Extract) testers are commonly used to detect ionic contamination from no-clean applications. Your comment rega