Electronics Forum | Tue May 04 14:42:58 EDT 1999 | Chrys Shea
| | I am about to embark on an effort to evaluate 3 different solder material suppliers and their recommended materials for our assembly process, in an effort to find the best supplier/material. We do mixed technology, with NOCLEAN chemistry so I wi
Electronics Forum | Mon May 10 07:53:48 EDT 1999 | Timothy O'Neill
| | | I am about to embark on an effort to evaluate 3 different solder material suppliers and their recommended materials for our assembly process, in an effort to find the best supplier/material. We do mixed technology, with NOCLEAN chemistry so I
Electronics Forum | Mon May 10 08:00:14 EDT 1999 | Timothy O'Neill
| | | | I am about to embark on an effort to evaluate 3 different solder material suppliers and their recommended materials for our assembly process, in an effort to find the best supplier/material. We do mixed technology, with NOCLEAN chemistry so
Electronics Forum | Tue Sep 18 07:52:29 EDT 2007 | davef
Does the change from supplier to supplier as a result of: * Board definition? * Differences in processing at fabs? 3 Specification Fir Tree General Technical Specification 3a Design/Layout: * IPC-2221 * IPC-2222 3b PCB Fab: * IPC-6011 * IPC-6012 * I
Electronics Forum | Thu May 02 10:25:14 EDT 2013 | wahahasteven
we have a Specialty coating system (SCS) precisoncoat spray coating system. we are using an acrylic coating material with about 80cp viscosity. The spraying pressure is around 4-6 psi. The main issue is the finish looking of the board. If we apply hi
Electronics Forum | Wed Mar 03 20:20:30 EST 1999 | Earl Moon
| We have recently had problems with bare boards coming in too thick. I would like to know how to properly specify the minimum and maximum thickness using the 13949F and IPC 4101 specs. (We currently use "MATERIAL: GFN 0620 C1/C1 A2A per MIL - P - 13
Electronics Forum | Thu Nov 11 17:17:11 EST 1999 | Boca
1. Most ionic testing is measured in NaCl, that is, the ionic residues are quantified in terms of NaCl equivalence. The test does not determine what the ionic residue is, just its relative strengh. 2. I use IPC cleanliness specs on OA fluxes but n
Electronics Forum | Wed Mar 06 21:16:17 EST 2002 | davef
�What does 5 micrograms of chloride mean to me?� * With SIR testing, you can show no detrimental leakage currents under humid conditions, no corrosion, no metal migration, which are the big factors in figuring out electrochemical reliability. People
Electronics Forum | Wed Nov 17 11:20:23 EST 1999 | Dave F
Hey Gyver: If you don�t mind (which you don�t have any choice about, because I�m going to do it anyhow, cause it�s MY word processor), I�m going to respond genericly, but still be directed to your question. Much of the following is paraphrased from
Electronics Forum | Tue Dec 29 03:35:10 EST 1998 | Earl Moon
| I am looking for a questionaire/list of items that need to be addressed to determine the pros/cons and equipment, manpower, cost and lead time to determine if one should consider setting up an in-house SMT line. | Can anyone help? | thanks | | L
IPC is the trade association for the printed wiring board and electronics assembly industries.