Electronics Forum | Tue Jun 04 20:34:28 EDT 2002 | russ
Jason, Excessive thermal ramp rates, misprints, improper pad design, paste type, placement pressure, all can cause solderballs. Do the pads on this board meet IPC 782 criterias? I have found that too much pad underneath component can cause this. A
Electronics Forum | Tue Jun 06 11:57:12 EDT 2006 | Chunks
IPC 610 says acceptable Class 1 (Class 2, 3 indicator) if they are entrapped/encpsulated balls within 0.13mm of lands or pads. or exceed 0.13mm in diameter. Defect Class 1,2,3: Solder ball violates min electrical clearance. Solder balls not entrap
Electronics Forum | Tue Sep 23 20:56:08 EDT 2008 | davef
For additional information, download IPC-7526 - Stencil and Misprinted Board Cleaning Handbook http://www.ipc.org/html/IPC-7526.pdf
Electronics Forum | Fri May 26 21:25:52 EDT 2006 | mika
Yes we do place "big and heavy" SMT DC/DC:s on most of our board's. Please tell us what brand it is or at least what the package look like?!? For instance we place a different numbers of "heavy" DC/DC converters (40x20mm & 45x25mm) that has the pick-
Electronics Forum | Thu Jan 24 19:57:40 EST 2002 | davef
Are there formalized standards for the properties of solder balls? No Get IPC-7095 �Design & Assembly Process Implementation for BGA's�. General comments about array package solder balls are: * Ceramic packages use harder solder, like 90/10. * Pla
Electronics Forum | Tue Jan 29 15:48:31 EST 2002 | davef
On his site "SMT In Focus", our friend Brian Sloth Blitzen lists the following sampling of lead-free [no lead] links: * Alpha Metals: http://www.alphametals.com/lead_free/index.html * Circuits Assembly magazine: http://www.circuitsassembly.com/db_ar
Electronics Forum | Mon Jul 16 15:49:33 EDT 2001 | Steve
The solder balls you are talking about are caused by too much paste. Reduce the size of the stencil aperatures. Concerning removing the solder balls, the first thing you need to ask yourself is, do I need to remove them. IPC-610, 12.4.10 states, "Ac
Electronics Forum | Thu Jun 19 21:39:31 EDT 2008 | mika
Hi, we used to have a RoHS package with uBGA 380 Solder ball's 0.8 mm pitch approx 15x15 mm, bump size is 0.4mm on a 0.33mm pad. Suddenly we need to use another vendor for various reasons. However, the new bump size is 0.45mm according to specs and t
Electronics Forum | Thu Nov 29 17:30:07 EST 2001 | davef
You give no clue of what you want to write about. Let's try this: J-STD-001, 8.3.1 Particulate Matter says words to the effect of solder balls / splats shall be neither: * Loose or able to be dislodged during normal service � NOR * Violate minimu
Electronics Forum | Thu Jul 19 08:00:03 EDT 2001 | doctord
Solder balls or mid chip beads? Remember IPC classification for Class 2 allows mid chip beads encapsulated in flux. Usually on R's and C's first thing I would do is verify .006 laser stencil 10% reduction and the most critical, The paste must be on t
IPC is the trade association for the printed wiring board and electronics assembly industries.