Electronics Forum | Tue Feb 08 19:44:31 EST 2005 | Dreamsniper
Is there IPC Standards that I could use with the following evaluation: a) Solder Paste Printing Performance b) Solder Paste Wetability What standards do you use or criteria when you evaluate solder paste with the above performance? thanks and r
Electronics Forum | Wed Mar 22 01:24:54 EST 2006 | Joseph
Dear all, Referring technical report from Vitronics Soltec, "Pad lifting, fillet lifting and fillet tearing issues in LF soldering". The use of LF solder alloys today has brought about a recurrence of this crack formation, called fillet tearing. The
Electronics Forum | Mon Jun 08 15:00:08 EDT 1998 | Earl Moon
| I work QA at an OEM in Alberta, Canada. I saw earlier posts on the smtnet regarding PCB haloing criteria. I am currently in a dispute with my PCB vendor over the acceptability of haloing (delamination) around plated through holes and vias on a lot
Electronics Forum | Thu May 17 07:36:40 EDT 2001 | Bob Willis
Here is a copy of a draft document on PIHR Inspection I have jotted down on a flight to Scotland yesterday, any comments suggestions etc ? I have already most of the photos for the standard but as you know there is nothing in the IPC document it just
Electronics Forum | Wed Oct 20 14:24:32 EDT 2004 | Steve Gregory
It all depends where the voids are, and that's tough to do with a transmission x-ray. One needs to be able tilt the assembly at 45-degrees during x-ray, so you can get an idea where the void is. Or, you spend some big bucks for an x-ray laminography
Electronics Forum | Wed Oct 20 14:44:24 EDT 2004 | Steve Gregory
It all depends where the voids are, and that's tough to do with a transmission x-ray. One needs to be able tilt the assembly at 45-degrees during x-ray, so you can get an idea where the void is. Or, you spend some big bucks for an x-ray laminography
Electronics Forum | Thu Apr 19 02:49:07 EDT 2007 | ray
I observed some black dot or some oxidation occured on chip termination on pcba reflowed fews weeks ago as buffer stock. The solder joint and fillet wetting is good and shinning. It is an acceptable or defect condition per IPC standard/requirement? W
Electronics Forum | Thu Oct 26 17:42:29 EDT 2000 | Philip A. Reyes
Hi Mr Paul! Thanks for answering my previous questions. Hope you can still accommodate my other queries. This is about the acceptable criteria of PBGA defects after reflow soldering. 1.What is the allowable (min and max. ball misregistration / misal
Electronics Forum | Tue Mar 17 08:20:59 EDT 2009 | scottp
I work for one of the largest automotive suppliers. Our Workmanship Standards pre-date IPC-610 but they are nearly identical in regards to solder balls. We supply to all the major OEMs, including the Japanese, and I don't recall our solder ball sta
Electronics Forum | Fri Aug 25 14:39:24 EDT 2006 | davef
1 When you peel the solder connection of a BGA, * If solder remains on the soldered surface [eg, component, substrate, etc], it's good. * If some solder remains and some base metal is present, it's marginal. * If no solder remains, it's NG. 2 Try I
IPC is the trade association for the printed wiring board and electronics assembly industries.
Training Provider / Events Organizer / Association / Non-Profit
3000 Lakeside Drive, 309 S
Bannockburn, IL USA
Phone: 847-615-7100