Electronics Forum | Fri Feb 06 18:32:59 EST 2015 | chsravan
Hi Scott,Thank you for the response. I was also thinking the same that the assembly will no longer be Class III. Thanks again.
Electronics Forum | Thu Feb 05 14:30:29 EST 2015 | chsravan
Can I apply IPC-610 class 3 workmanship standards to an assembly made with a IPC-600 class 2 PCB?
Electronics Forum | Fri Feb 06 11:11:04 EST 2015 | mascott123
I have asked that same question to a co-chair of the J-STD-001 committee who in turn checked with personnel at IPC. The answer I received is that yes you can apply the Class 3 assembly requirements using a class 2 PWB but the resultant assembly will
Electronics Forum | Mon Sep 25 11:43:56 EDT 2006 | mrduckmann2000
HELP, I AM SEEKING THE PROPER CANDLE POWER FOR A SHOP FLOOR THAT IS WORKING TO IPC-610 CLASS II AND III STANDARDS. ANYONE KNOW WHAT THE MIN AND MAX SHOULD BE??? THANKS FOR THE HELP!
Electronics Forum | Mon Sep 26 12:58:33 EDT 2011 | action_101
So you are saying that building to class III is going to prevent failures? I disagree. Class III is trying to hit target condition in every aspect of the production of the circuit board. That my friend does not ensure failures from happening. I see
Electronics Forum | Fri Jan 26 16:24:10 EST 2007 | Bob R.
Whether there's a fillet or not depends on the component type. Most have a fillet but some, such as QFN's, don't necessarily have one. Have a look at IPC-610D Workmanship Standards to understand when you should expect one and when you shouldn't. T
Electronics Forum | Fri Sep 23 16:39:00 EDT 2011 | action_101
The small investemnt of purchasing the IPC-610 manual will pay for itself very quickly. A brief description of the two classes in a few words would be the following: Class II - a well built product with reasonable expectations for both the manufactur
Electronics Forum | Sat Jul 17 13:25:02 EDT 1999 | Scott
| | | | | | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | | | | | | | | | What is it you're tr
Electronics Forum | Mon Nov 02 07:16:47 EST 2009 | umar
Base on the top picture condition, seems like the boards condition is a lot with solder splash or solder ball which is per IPC-610 is under reject (under 5.6.2)for class 3 product. While the picture 2 is showing those the solder resist is not melt pr
Electronics Forum | Wed Feb 24 07:56:53 EST 1999 | Brian C
Under IPC-A-610 Section 10.3(Components on their sides) it reads: ______________________________________________________ Acceptable - Class 1,2 Nonconforming Defect � Class 3 Chip components on its side provided the following are met: Chip