Electronics Forum | Mon Jul 24 07:18:51 EDT 2017 | jamesbarnhart
IPC has updated assembly standards for IPC A-610 and IPC JSTD-001 making them easier to use and adding information in areas that have evolved. Both IPC J-STD-001E and IPC-A-610E have also been more closely linked to eliminating the differences that c
Electronics Forum | Fri Dec 12 13:49:38 EST 1997 | Richard
Check out the IPC J-Std 001B
Electronics Forum | Tue Jan 30 18:29:41 EST 2007 | realchunks
Sad part is THEY specified IPC J-STD-001C!!!
Electronics Forum | Fri Aug 30 22:51:14 EDT 2013 | cvogel
IPC-J-STD-001E in regards to Ionic Cleanliness standards states less than 1.56 µg/cm² of total NaCL. Assuming a typical electronic process which involves smt, wave, and post-hand soldering and uses NO-Clean flux throughout all process, is it typi
Electronics Forum | Tue Sep 06 12:41:52 EDT 2016 | kmclain
IPC J-STD-001 does not allow solder inspection to be combined with coating inspection for classes 2 and 3.
Electronics Forum | Mon Feb 21 20:15:49 EST 2022 | arminski
since IPC-J-STD-001 RevH obsoleted the 1.56ug/cm2 UCL of ionic contamination tester in testing using ROSE test, how do you define the acceptable limit per PCB assembly? thanks
Electronics Forum | Tue Feb 24 18:21:52 EST 1998 | Graham Naisbitt
You should refer to the IPC-J-STD001B and IPC-TM-650, they will give you good recommendations. Also, we do new reliability test systems and if you can give me your address and e-mail, I will send you some more info. Regards, Graham Naisbitt | looking
Electronics Forum | Mon Jul 24 09:15:32 EDT 2017 | davef
James: This is not "breaking news." IPC-A-610F, Acceptability of Electronic Assemblies was released in July 2014. Both, ... * IPC-A-610G, Acceptability of Electronic Assemblies * J-STD-001G, Requirements for Soldered Electrical and Electronic Assem
Electronics Forum | Mon Jul 14 07:49:50 EDT 2008 | edmaya33
Do we really need to follow the IPC J-STD-001 Solder purity? If so, how to effectively balance the chemistry of Sn63/Pb37 other than adding a pure tin on the solder bath? Is this really needed to monitor in monthly basis?How many kgs of pure tin pe
Electronics Forum | Thu Sep 05 22:36:38 EDT 2013 | davef
Yes, providing your: * Inbound material does not compromise your process. * Soldering processes apply the proper amount of flux and activate it properly * Material handling does not contaminate your boards Recognize that the IPC requirements of less