Electronics Forum | Tue Jul 19 04:44:52 EDT 2016 | pavel_murtishev
Hello, Unfortunately I have lost my hard copy of "Soldering in electronics" by R. J. Klein Wassink. Is it possible to purchase electronic copy of the book on the net? Having googled a couple of hours, I have found nothing. Any input is highly appr
Electronics Forum | Tue Jul 19 08:48:34 EDT 2016 | davef
Hi Pavel … Sad that you lost your "Soldering In Electronics" by R. J. Klein Wassink Points are: * According to Google Books, there is no eBook [https://books.google.com/books/about/Soldering_in_Electronics.html?id=P1aaAAAAIAAJ]. * Publisher: Elect
Electronics Forum | Mon May 08 17:19:52 EDT 2000 | John Thorup
Hello Steve Most of these are available from the SMTA bookstore in Minnesota. 612/920-7682 www.smta.org There is a discount if you are a member and they offer free UPS ground shipping. Cast my vote for Klein-Wassink John Thorup
Electronics Forum | Tue Dec 14 03:26:09 EST 1999 | Chris May
Steve, Two good reference books to have are 1) SMT Soldering Handbook by Rudlof Strauss (ISBN 0-7506-3589-4) 2) Soldering In Electronics by R.J. Klein Wassink( ISBN 0-901150-24-x) Regards, Chris
Electronics Forum | Fri Oct 22 05:02:58 EDT 1999 | Chris May
John, Have a look in Farnell page 1896 pt. No. 198-870 @ �50.00 SMT Soldering Handbook. OR for the "Bible", try to source "Soldering in Electronics" by R.J. Klein Wassink. Regards, Chris.
Electronics Forum | Sat Feb 02 09:33:33 EST 2002 | davef
�8.4.2, Cracking Of Soldered Joints in the epic "Soldering In Electronics" by RJ Klein Wassink [Electrochemical Publications,ISBN 0 901150 24 X] covers cracking differented by: * Overloading * Creep * Fatigue You can't go wrong by starting there.
Electronics Forum | Thu Feb 12 21:30:45 EST 2004 | davef
Comments are: * We're amazed that you can thermocompression bond to epoxy. * Silver may be oxidizing during expoxy cure. * Klein Wassink talks about aging in THE BOOK [Soldering in Electronics: A Comprehensive Treatise on Soldering Technology for Sur
Electronics Forum | Mon May 21 10:06:54 EDT 2007 | patrickbruneel
Dave, Thanks a lot; you truly are a living database. I will need new spectacles missed the eutectic alloy in table 4.8 of the Klein Wassink book.
Electronics Forum | Tue Jun 13 12:03:10 EDT 2000 | Chris May
Jason, If 225C is the topside temp of your board just prior to hitting the wave, I would say this is too high. Your flux suppliers data sheet should tell you an ideal topside temp for good flux activation, probably around 190C. According to the Bi
Electronics Forum | Thu May 24 19:19:20 EDT 2001 | davef
Try: * Poor looking solder connections * Good looking solder connections * Reliable solder connections Look to Ch 5 of "Manufacturing Techniques For Surface Mounted Assemblies"; RJ Klein Wassink & MMF Verguld; Electrochemical Pub; ISBN 0-901150-30-4