Electronics Forum | Fri Jun 06 07:34:43 EDT 2003 | johnw
Rick, my understanding is that the US do not have plan's fr lead free legislation. However the European legislation states that any product entering the european market after June 2006 must meet the lead free std's of the directive. So basically if
Electronics Forum | Wed May 24 16:47:21 EDT 2006 | patrickbruneel
Inds, It's about time that lead-free components can stand higher temps "myth" stops. The only difference is the plating, the component itself has not changed. Can you give us an update on this threat? If you�re the same inds http://www.smtnet.com//
Electronics Forum | Fri Jan 27 18:32:15 EST 2006 | mafc65
Well, most of the capacitor are thru hole, then pcb's goes to adhesive process upsidedown to continue SMT process in which , maximun tempetarure is 120�, so temperature is not problem. About SMT capacitorS, I will check temperature specs before mount
Electronics Forum | Fri Jan 27 15:12:48 EST 2006 | GS
From technical point of view: it should not be a problem to mix Pb with Pb Free components soldered with a LF solder process. You have to take care about the max temperature allowed on your Pb components and make sure they can withstand the higher
Electronics Forum | Wed Jul 27 15:54:44 EDT 2005 | Hiram
Hi everybody, We have wave solder fixtures made of Durapol and multiple wave solder machines. Most likely we�ll use the same pallets for either tin-lead or lead-free solder for a while (of course after washing the pallets). Should we test the palle
Electronics Forum | Wed Jul 27 16:27:57 EDT 2005 | GS
It may be you should look for higher TG of Durapol Rgds GS
Electronics Forum | Wed Jul 27 22:09:49 EDT 2005 | Ken
My policy is not to mix them. You have zero cross contamination potiental with this policy.
Electronics Forum | Tue Dec 04 09:48:43 EST 2001 | davef
Defining the thickness of solder between the lead and the pad, J-001 states "Properly wetted fillet shall be evident." J-001 is available from http://www.ipc.org. Factors that affect this are: * Amount and composition of solder * Amount and compo
Electronics Forum | Tue Jun 03 12:24:50 EDT 2003 | blnorman
I have received information from the European Commissioners Environmental group that automotive electronics are not covered by WEEE (waste electrical and electronic equipment 2002/96/EC) or RoHS (reduction of hazardous substances 2002/95/EC) because
Electronics Forum | Thu Jun 05 16:44:19 EDT 2003 | blnorman
The data we have is from an IBM report. Below 100�C the SAC reliability is almost double that of SnPb (-40 to 100�C thermal cycle). When the upper end temp is increased to 125�C the reliability drops to 75% of SnPb. I'd like to see the data that s