Electronics Forum | Thu Feb 16 12:41:50 EST 2006 | fredericksr
Hey folks, I was interested in any information that you might have on tombstone reduction when using a lead free solder and profile. Thanks for any input that you may have! -Russ #x
Electronics Forum | Fri Feb 17 09:02:21 EST 2006 | russ
proper pad geometries, accurate placement, and good reflow profile. Are you having problems right now?
Electronics Forum | Fri Feb 17 11:01:47 EST 2006 | amol_kane
with lead-free solders, one would expect to find less instances of tombstoning. this is because SAC alloys are not eutectic and melt over a range of temp (usually 217-220 deg C) instead of at a single temperature. therefore the forces due to solder s
Electronics Forum | Wed Jan 07 12:09:40 EST 2004 | Kris
Hi All, Does any body have any information on hot bar lead free soldering ? Need papers or experimental data ASAP Thanks
Electronics Forum | Tue Aug 31 12:01:26 EDT 2004 | russ
Kris, this practice has gone on for years. I have never heard of any problems associated with this. I have heard "grumblings" about tin lead parts being processed with lead free paste, but have seen or heard of no data to support. Russ
Electronics Forum | Tue Aug 31 11:57:03 EDT 2004 | Kris
Hi Any body have any issues soldering tin lead solder paste with lead free terminations ? Components are leaded devices and chip components have read the theoritical discussions on the forum, need to know if any body has seen any real issues tod
Electronics Forum | Tue Aug 31 19:50:44 EDT 2004 | davef
To take our turn at keeping everyone else on the straight and narrow. For more on lead contamination of no-lead solder, look here: http://www.aimsolder.com/techarticles/Lead%20Contamination%20in%20Lead-Free%20Electronics%20Assembly.pdf [We apolog
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Tue Aug 31 21:45:49 EDT 2004 | KEN
I have experienced this directly in SMT and wave solder. Fillet lift (can) be a direct indicator to lead enrichment (but its not the exclusive symptom). Lead enrichment in smt joints reduces the interfacial strength shortening the time to creep f